A type of TiO/bamboo charcoal composite made by a dip-dry method was loaded onto wood veneer with a vacuum- pressure method in order to prepare modified poplar veneer. The pore structure parameters and surface morphology of the TiO2/ bamboo charcoal composite were determined and analyzed by means of a porosimetry analyzer and SEM. The results show that the surface morphology of the composite does not change after being loaded with nano TiO2. However, its specific surface area （359.814 m^2·g^-1）, pore volume （0.317 cm^3.g^-1） and average pore diameter （3.526 nm） increased; particularly the cumulative volume of pores was increased by 65.83%. In addition, the distribution range of the pores was wider than that of the bamboo charcoal. Combining the SEM of unmodified and modified poplar veneer, the results of X-ray photoelectron spectroscopy revealed that actually some TiOz compounds, i.e., 4.08%, are imbedded in the modified poplar veneer.
A type of TiO/bamboo charcoal composite made by a dip-dry method was loaded onto wood veneer with a vacuum- pressure method in order to prepare modified poplar veneer. The pore structure parameters and surface morphology of the TiO2/ bamboo charcoal composite were determined and analyzed by means of a porosimetry analyzer and SEM. The results show that the surface morphology of the composite does not change after being loaded with nano TiO2. However, its specific surface area （359.814 m^2·g^-1）, pore volume （0.317 cm^3.g^-1） and average pore diameter （3.526 nm） increased; particularly the cumulative volume of pores was increased by 65.83%. In addition, the distribution range of the pores was wider than that of the bamboo charcoal. Combining the SEM of unmodified and modified poplar veneer, the results of X-ray photoelectron spectroscopy revealed that actually some TiOz compounds, i.e., 4.08%, are imbedded in the modified poplar veneer.
基金
A Project Funded by the Priority Academic Program Development of Jiangsu Higher Education Institutions for financial support to conduct this research