摘要
Boron-doped nano-crystalline diamond （NCD） thin films have been successfully deposited on well-polished poly-crystalline diamond （PCD） thick films in a microwave plasma enhanced chemical vapor deposition （MPCVD） reactor for the first time. Different surface pretreatment techniques are carried out under different gas conditions （CH4, H2, Ar, and CH4/H2） to eliminate the effect of grain boundaries on the growth of a smooth NCD intrinsic layer. Well doped NCD films have been fabricated in CH4/H2/B2H6 plasma by varying the atomic ratio of B/C and the substrate temperature. Atomic force microscopy （AFM） results show that pretreatment in pure CH4 plasma at 1000℃ is most effective for NCD growth, while hydrogen containing plasma is harmful to the surface smoothness of NCD thin fihns. Doping research indicates that the optimum parameters for the boron-doping of high-quality NCD thin films are B/C=300 ppm （10-6） and 800℃.
Boron-doped nano-crystalline diamond （NCD） thin films have been successfully deposited on well-polished poly-crystalline diamond （PCD） thick films in a microwave plasma enhanced chemical vapor deposition （MPCVD） reactor for the first time. Different surface pretreatment techniques are carried out under different gas conditions （CH4, H2, Ar, and CH4/H2） to eliminate the effect of grain boundaries on the growth of a smooth NCD intrinsic layer. Well doped NCD films have been fabricated in CH4/H2/B2H6 plasma by varying the atomic ratio of B/C and the substrate temperature. Atomic force microscopy （AFM） results show that pretreatment in pure CH4 plasma at 1000℃ is most effective for NCD growth, while hydrogen containing plasma is harmful to the surface smoothness of NCD thin fihns. Doping research indicates that the optimum parameters for the boron-doping of high-quality NCD thin films are B/C=300 ppm （10-6） and 800℃.
基金
supported by National Natural Science Foundation of China(No.11175137)
the Research Fund of Hubei Provincial Department of Education of China(No.Q20081505)
the Research Fund of Wuhan Institute of Technology of China(No.11111051)