摘要
利用分子自组装膜技术制备了有机硅烷 /纳米 Ti O2 复合膜 ,并用 XPS进行了表征 .摩擦磨损试验结果表明 ,硅烷自组装膜可以降低基片的摩擦系数 ,但其强度较弱 ,这可能是由于硅烷与基片的结合强度较弱、硅烷碳链较短以及硅烷在基片上的自组装不太致密有关 .硅烷 /Ti O2 复合膜的摩擦系数比硅烷自组装膜的摩擦系数小 ,而且耐磨寿命大幅度提高 .摩擦 50次以后 ,硅烷 /Ti O2 复合膜的摩擦系数突然增大并超过干净基片的摩擦系数 ,这可能是由于 Ti
Ultrathin film composed of titanium dioxide and silicone coupling reagent molecules has been fabricated on single crystal silicon by molecular self assembly process. X ray photoelectron spectroscopy (XPS) analysis shows that composite film was successfully prepared. The results of friction and wear test show that the composite self assembly film can decrease the friction coefficient of single crystal silicon significantly. However, the strength of the composite film is not good.