The effect of Cu addition on crystallization behavior and soft magnetic properties of Fe 84xP10C6 Cux (x= 0 1.15) alloys was investigated. Low-cost FePCCu nanocrystalline alloys dispersed with α-Fe phase with an average grain size of 15-35nm were obtained by appropriately annealing the melt-spun ribbons at 683K for 5min. The Fe 83.25P10C6Cu0.75 nanocrystalline alloy exhibits a high B s of 1.65T, low H c of 3.3A/m and high eat 1kHz of21 100, which is superior to the traditional FePC soft magnetic alloys. The core loss is as low as 0.32W/kg at1.0 T and 50Hz, which is 60% that of nonoriented Fe 6.5 mass% Si-steel. It is encouraging to synthesize this Fe-based nanocrystalline alloy with excellent soft-magnetic properties even using commercially industry-grade raw materials, which is promising for the future industrial applications.
The effect of Cu addition on crystallization behavior and soft magnetic properties of Fe84-xP10C6Cux (x = 0-1.15) alloys was investigated. Low-cost FePCCu nanocrystalline alloys dispersed with ct-Fe phase with an average grain size of 15-35 nm were obtained by appropriately annealing the melt-spun ribbons at 683 K for 5 min. The Fe83.25P10C6Cu0.75 nanocrystalline alloy ex- hibits a high Bs of 1.65 T, low Hc of 3.3 A/m and high μc at 1 kHz of 21 100, which is superior to the traditional FePC soft magnetic alloys. The core loss is as low as 0.32 W/kg at 1.0 T and 50 Hz, which is 60% that of nonoriented Fe 6.5 mass% Si-steel. It is encouraging to synthesize this Fe-based nanocrystalline alloy with excellent soft-magnetic properties even using commercially industry-grade raw materials, which is promising for the future industrial applications.
基金
supported by the National High Technology Research and Development Program of China ("863" Program) (Grant No.2009AA03Z214)
the National Science Fund of China for Distinguished Young Scholars (Grant No. 50825103)
the National Natural Science Foundation of China (Grant No. 51001112)
the "Hundred of Talents Program" (Grant No. KGCX-2-YW-803) by Chinese Academy of Sciences