The effect of lime on the pre-desilication and digestion of gibbsitic bauxite in synthetic sodium aluminate liquor at different tem- peratures was investigated. The bauxite is comprised of gibbsite, aluminogoethite, hematite, kaolin, quartz, and minor boehmite. Lime in- creases the desilication efficiency of the bauxite during the pre-desilication process by promoting the conversion of sodalite and cancrinite to hydrogamet. Desilication reactions during the digestion process promoted by lime result in the loss of A1203 entering the red mud, but the amount of aluminogoethite-to-hematite conversion promoted by lime leads to the increase of aluminogoethific A1203 entering the digested liquor. The alumina digestion rate at 245~C is higher than that at 145 C due to the more pronounced conversion of aluminogoethite to hema- tite. The soda consumption during the digestion process decreases due to lime addition, especially at higher temperatures.
The effect of lime on the pre-desilication and digestion of gibbsitic bauxite in synthetic sodium aluminate liquor at different tem- peratures was investigated. The bauxite is comprised of gibbsite, aluminogoethite, hematite, kaolin, quartz, and minor boehmite. Lime in- creases the desilication efficiency of the bauxite during the pre-desilication process by promoting the conversion of sodalite and cancrinite to hydrogamet. Desilication reactions during the digestion process promoted by lime result in the loss of A1203 entering the red mud, but the amount of aluminogoethite-to-hematite conversion promoted by lime leads to the increase of aluminogoethific A1203 entering the digested liquor. The alumina digestion rate at 245~C is higher than that at 145 C due to the more pronounced conversion of aluminogoethite to hema- tite. The soda consumption during the digestion process decreases due to lime addition, especially at higher temperatures.
基金
the National Natural Science Foundation of China(Nos.51104041 and 51174054)