硬质合金表面电沉积Ni/Ni-MoS_2自润滑涂层的研究

Electro Deposition of Ni/Ni-MoS_2 Self-lubricating Coating on Cemented Carbide

采用电沉积方法在YT14硬质合金表面制备Ni/Ni-MoS2自润滑涂层,研究电流密度、pH值、MoS2加入量对自润滑沉积速率和涂层中MoS2含量的影响。结果表明:随着电流密度、pH值、MoS2加入量的增加,沉积速率和涂层中MoS2的含量都呈现先增加,后下降的规律;电流密度达到3.5 A/dm2时,沉积速率达到最大,电流密度为2 A/dm2时,MoS2的含量最高;在pH值约为4.5时,涂层的沉积速率和涂层中MoS2的含量达到最大值;当MoS2加入量为28g/L时,沉积速率达到最大值为0.812μm/min,涂层中MoS2的质量分数达到最大值为3.26%。

Ni/Ni-MoS2 self-lubricating coatings were prepared on cemented carbide by electro deposition. The effects of current density,pH value, MoS2 concentration of the plating liquid on deposition rate and MoS2 content in coatings were studied. The results indicate that the deposition rate and MoS2 content in coatings are firstly increased and then decreased with the increase of current density, pH value, MoS2 concentration of the plating liquid. The max value of deposition rate, and the max value of MoS2 content in the coatings are reached at the current of 3.5 A/din2 and 2 A/dm2, separately. The max value of deposition rate and MoS2 content in the coatings are reached at the pH value of 4. 5. The max deposition rate of 0. 812 μm/min,and the max MoS2 content of 3.26% are reached when the MoS2 concentration is 28 g/L.