摘要
The crystallization, microstructure, and soft magnetic properties of Fe52Co34Hf7B6Cul alloy are studied. Amorphous Fe52Co34Hf7B6Cul alloys are first treated by a pulsed magnetic field with a medium frequency, and then annealed at 100 ℃-400 ℃ for 30 min in a vacuum. The rise in temperature during the treatment by a pulsed magnetic field is measured by a non-contact infrared thermometer. The soft magnetic properties of specimens are measured by a vibrating sample magnetometer （VSM）. The microstructure changes of specimens are observed by a MSssbauer spectroscopy and transmission electron microscope （TEM）. The results show the medium-frequency pulsating magnetic field will pro- mote nanocrystallization of the amorphous alloy with a lower temperature rise. The nanocrystalline phase is （α-Fe（Co） with bcc crystal structure, and the grain size is about 10 nm. After vacuum annealing at 100 ℃ for 30 min, scattering nanocrystalline phases become more uniform, the coercive force and the saturation magnetization of the specimens are 41.98 A/m and 185.15 emu/g.
The crystallization, microstructure, and soft magnetic properties of Fe52Co34Hf7B6Cul alloy are studied. Amorphous Fe52Co34Hf7B6Cul alloys are first treated by a pulsed magnetic field with a medium frequency, and then annealed at 100 ℃-400 ℃ for 30 min in a vacuum. The rise in temperature during the treatment by a pulsed magnetic field is measured by a non-contact infrared thermometer. The soft magnetic properties of specimens are measured by a vibrating sample magnetometer （VSM）. The microstructure changes of specimens are observed by a MSssbauer spectroscopy and transmission electron microscope （TEM）. The results show the medium-frequency pulsating magnetic field will pro- mote nanocrystallization of the amorphous alloy with a lower temperature rise. The nanocrystalline phase is （α-Fe（Co） with bcc crystal structure, and the grain size is about 10 nm. After vacuum annealing at 100 ℃ for 30 min, scattering nanocrystalline phases become more uniform, the coercive force and the saturation magnetization of the specimens are 41.98 A/m and 185.15 emu/g.
基金
Project supported by the National Natural Science Foundation of China(Grant No.50771025)