Platinum （Pt） implants coated with poly （3, 4-ethylenedioxythiophene）/carbon nanotube （PEDOT/CNT） composite films were implanted into the brain of rats, and the brain response was evaluated 6 weeks after the implantation. The surface morphology of Pt implants with and without the PEDOT/CNT coating was studied using scanning electron microscopy （SEM）. After 6 weeks post-implantation, the expression of laminin （vascular endothelial marker） and neuronal nuclei （NeuN, neuronal marker） were evaluated by immnohistochemistry. It is revealed that the obvious improvements of the surface density of blood vessels and neurons aound the Pt implants with the coating, which were evidenced by laminin and NeuN staining in the zone within the distance of 150 μm to the implant interface. These results suggest the PEDOT/CNT composite films can improve the biocompatibility of the Pt electrodes while it is implanted in brain.
Platinum （Pt） implants coated with poly （3, 4-ethylenedioxythiophene）/carbon nanotube （PEDOT/CNT） composite films were implanted into the brain of rats, and the brain response was evaluated 6 weeks after the implantation. The surface morphology of Pt implants with and without the PEDOT/CNT coating was studied using scanning electron microscopy （SEM）. After 6 weeks post-implantation, the expression of laminin （vascular endothelial marker） and neuronal nuclei （NeuN, neuronal marker） were evaluated by immnohistochemistry. It is revealed that the obvious improvements of the surface density of blood vessels and neurons aound the Pt implants with the coating, which were evidenced by laminin and NeuN staining in the zone within the distance of 150 μm to the implant interface. These results suggest the PEDOT/CNT composite films can improve the biocompatibility of the Pt electrodes while it is implanted in brain.
基金
Funded by the High Tech Research and Development ("863") Program of China (2006AA02Z4E6)
the National Natural Science Foundation of China (Nos. 21073136, 81271364)