OTS自组装单分子膜在玻璃表面形成过程的AFM研究 被引量:18

Formation of OTS Self-assembled Monolayer on Glass Surface Investigated by AFM
下载PDF
导出
摘要 运用原子力显微镜研究了十八烷基三氯硅烷在玻璃表面自组装形成单分子膜的过程 .通过对样品表面的显微图像、表面平均粗糙度及前进接触角的测量分析 ,揭示了自组装单分子膜在玻璃表面的生长规律 。 By using AFM, the process of the OTS monolayer formation on glass substrate surface by self assembly from 1×10 -3 mol/L OTS toluene solution at 18 ℃ was revealed. The analyses of AFM images as well as the surface mean roughness R a of the sample surfaces indicated that, after 15 min reaction a smooth OTS monolayer with a R a of 0.156 nm/4 μm 2 could be obtained on the glass surface. However, this freshly formed OTS monolayer was unstable, as the reaction proceeds, the R a of the monolayer would slightly increase within the succeeding 15 min, and finally keep a constant value about 0.170 nm/4 μm 2 even for 2 h reaction. The advancing contact angle measurement showed that after ~15 min reaction, a completely hydrophobic surface formed with an advancing contact angle of 105°. Our research also showed that during the initial reaction period, most of the adsorption molecules just adsorbed on the substrate surface physically. But some kinds of very strong combination between a few of adsorption molecules and the substrate surface was established, which was much stronger than physical interaction.
出处 《高等学校化学学报》 SCIE EI CAS CSCD 北大核心 2000年第8期1257-1260,共4页 Chemical Journal of Chinese Universities
基金 国家教育部留学归国人员科研启动基金
关键词 自组装单分子膜 原子力显微镜 OTS 玻璃表面 Octadecyltrichlorosilane(OTS) Self assembled monolayer Atomic force microscope(AFM)
  • 相关文献

参考文献3

  • 1Xiao X D,Langmuir,1995年,11卷,5期,1600页
  • 2Gun J,J Colloid Interface Sci,1986年,112卷,2期,457页
  • 3Gun J,J Colloid Interface Sci,1984年,101卷,1期,201页

同被引文献202

引证文献18

二级引证文献111

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部