摘要
在乙醇体系中采用十八硫醇(ODT)在青铜表面制备自组装膜(SAMs),采用循环伏安法、极化曲线和交流阻抗谱等电化学方法研究该膜在0.5 mol/LNaCl溶液中对青铜电极的缓蚀性能。结果表明:ODT在青铜表面形成了SAMs,能够有效抑制青铜的腐蚀。随着成膜温度和ODT浓度的增高,ODT自组装膜的缓蚀效率和覆盖度提高。当ODT浓度为0.1 mol/L、成膜温度为60℃时,缓蚀效率为98.1%,覆盖度为98.7%;十八硫醇在青铜表面的吸附行为符合Langmuir吸附等温式,吸附机理是典型的化学吸附。
The self-assembled monolayers(SAMs) were prepared on bronze surface in ethanol solution using octadecanethiol(ODT).The effect of the membrane on the corrosion inhibition of bronze electrode in 0.5 mol/L NaCl solution was investigated by using cyclic voltammetry(CV),polarization curve,and electrochemical impedance spectroscopy(EIS).The results show that the ODT can be assembled on the surface of bronze electrode to form monomolecular SAMs,which can prevent effectively the corrosion of bronze.The higher the concentration of ODT and temperature are,the more excellent the inhibition efficiency and the denser the coverage degree are.When the concentration of ODT is 0.1 mol/L and temperature is 60 ℃,the inhibition efficiency reaches 98.1% and the coverage degree reaches 98.7%.The adsorption of ODT SAMs follows the Langmuir's adsorption isotherm formula,and the adsorption mechanism is of typical chemical adsorption.
出处
《中国有色金属学报》
EI
CAS
CSCD
北大核心
2012年第11期3249-3254,共6页
The Chinese Journal of Nonferrous Metals
基金
江苏高校优势学科建设工程资助项目
关键词
十八硫醇
青铜
自组装膜
缓蚀
吸附
octadecanethiol
bronze
self-assembly monolayer
anticorrosion
adsorption