In this article, our recent progress concerning the effects of atomic substitution, magnetic field, and temperature on the magnetic and magnetocaloric properties of the LaFe13-xAlx compounds are reviewed. With an increase of the aluminum content, the compounds exhibit successively an antiferromagnetic （AFM） state, a ferromagnetic （FM） state, and a mictomagnetic state. Furthermore, the AFM coupling of LaFe13 -xAlx can be converted to an FM one by substituting Si for A1, Co for Fe, and magnetic rare-earth R for La, or introducing interstitial C or H atoms. However, low doping levels lead to FM clusters embedded in an AFM matrix, and the resultant compounds can undergo, under appropriate applied fields, first an AFM-FM and then an FM-AFM phase transition while heated, with significant magnetic relaxation in the vicinity of the transition temperature. The Curie temperature of LaFe13-xAlx can be shifted to room temperature by choosing appropriate contents of Co, C, or H, and a strong magnetocaloric effect can be obtained around the transition temperature. For example, for the LaFel 1.5All.5Co.2Hl.o compound, the maximal entropy change reaches 13.8 J.kg-1.K-1 for a field change of 0-5 T, occurring around room temperature. It is 42% higher than that of Gd, and therefore, this compound is a promising room-temperature magnetic refrigerant.
In this article, our recent progress concerning the effects of atomic substitution, magnetic field, and temperature on the magnetic and magnetocaloric properties of the LaFe13-xAlx compounds are reviewed. With an increase of the aluminum content, the compounds exhibit successively an antiferromagnetic （AFM） state, a ferromagnetic （FM） state, and a mictomagnetic state. Furthermore, the AFM coupling of LaFe13 -xAlx can be converted to an FM one by substituting Si for A1, Co for Fe, and magnetic rare-earth R for La, or introducing interstitial C or H atoms. However, low doping levels lead to FM clusters embedded in an AFM matrix, and the resultant compounds can undergo, under appropriate applied fields, first an AFM-FM and then an FM-AFM phase transition while heated, with significant magnetic relaxation in the vicinity of the transition temperature. The Curie temperature of LaFe13-xAlx can be shifted to room temperature by choosing appropriate contents of Co, C, or H, and a strong magnetocaloric effect can be obtained around the transition temperature. For example, for the LaFel 1.5All.5Co.2Hl.o compound, the maximal entropy change reaches 13.8 J.kg-1.K-1 for a field change of 0-5 T, occurring around room temperature. It is 42% higher than that of Gd, and therefore, this compound is a promising room-temperature magnetic refrigerant.
基金
Project supported by the National Natural Science Foundation of China
the Key Research Program of the Chinese Academy of Sciences
the National Basic Research Program of China
the National High Technology Research and Development Program of China