摘要
以经焙烧处理的菱镁石作为含MgO添加剂生产氧化球团,考察了MgO含量对氧化球团抗压强度的影响.研究表明:随着球团矿中MgO含量的增加,球团矿的抗压强度逐渐下降.其主要原因为:球团中MgO含量的增加使得球团中Fe3O4氧化成Fe2O3再结晶过程减弱,连晶不完全,且分布不均,不利于球团矿的固结;通过对不同MgO含量的球团矿的孔隙分布及孔隙度分析可知,随着球团矿中MgO含量的增加,球团矿的孔径及孔隙度逐渐增大,导致球团矿的抗压强度不断下降.
The caustic calcined magnesite was used as an additive to produce an oxidized pellet.The effect of MgO-bearing on the compressive strength of pellet was investigated.The results showed that with the addition of MgO-bearing in pellet,the compressive strength of pellet decreases gradually.The reasons as follows:(1)the MgO makes against the recrystallization of Fe2O3 after Fe3O4 is oxidized to Fe2O3.The recrystallization of Fe2O3 is fainter,the crystallite is maldistributed and the consolidation of pellet is incomplete;(2)according to the pore space analysis of different MgO-bearing in pellets,with the addition of MgO-bearing in pellet,the porosity and aperture increase,leading to the decreasing of compressive strength of pellet.
出处
《东北大学学报(自然科学版)》
EI
CAS
CSCD
北大核心
2013年第1期103-106,共4页
Journal of Northeastern University(Natural Science)
基金
国家自然科学基金资助项目(51074040)
关键词
氧化球团
抗压强度
显微结构
孔隙分布
孔隙度
oxidized pellet
compressive strength
microstructures
pore distribution
porosity