研究了β-AI2O3粉体材料的制备工艺与性质迪种粉体材料可以采用慢速升温、分阶段保温的工艺,煅烧Li2CO3、Na2CO3、AI2O3的均匀混合物不经球直接制得,根据使用要求与生产5条件,混合物可用干混、兰湿混-过筛或喷雾干燥法来制备、粉体材料主要由β/β"-AI2O3组成,β"相的相对含量〉70%,加入适当的粘结剂与溶剂,可将其制臧在气环境中金属管道外的固体电解质涂层。
β-Al_2O_3 powdered material could be prepared from the mixtures of Li_2CO_3, Na_2CO_3 and AL_2O_3, which were obtained by dry mixing, wet mix-screening or spray-drying process, by stepped calculating without grinding. The effect of preparation condition on the properties of the powdered material was showed. The powder composed of β/β'-Al_2O_3 in principle, f(β~')>70%, could be fabricated into solid electrolytic coating for metal pipeline in atmosphere, with some binders and solvents. The powder in the coating wus stable chemically and electrochemically to metal, binders and moistur. The polarization behavior of cathode for 'Beta-coating' showed that there was a flat at the polarization curve, which could be evajuated for the cathode protection of metal in atmosphere.
出处
《无机材料学报》
SCIE
EI
CAS
CSCD
北大核心
2000年第4期704-710,共7页
Journal of Inorganic Materials
关键词
粉体材料
固固电解质
阴极保护
三氧化二铝
金属
β-Al_2O_3
powdered material
solid electrolytic coating
cathode protection