Influence of masticatory fatigue on the fracture resistance of the pulpless teeth restored with quartz-fiber post-core and crown 被引量:10

Influence of masticatory fatigue on the fracture resistance of the pulpless teeth restored with quartz-fiber post-core and crown
下载PDF
导出
摘要 To investigate whether masticatory fatigue affects the fracture resistance and pattern of lower premolars restored with quartz-fiber post-core and full crown, 44 single rooted lower premolars recently extracted from orthodontic patients were divided into two groups of 22 each. The crowns of all teeth were removed and endodontically treated and then restored with quartz-fiber post-core and full crown. Twenty-two teeth in one group were selected randomly and circularly loaded at 45° to the long axis of the teeth of 127.4 N at a 6 Hz frequency, and the other group was not delivered to cyclic loading and considered as control. Subsequently, all teeth in two groups were continually loaded to fail at 45° to the long axis of the teeth at a crosshead speed of 1 mm.min-1. The mean destructive force values were (733.88±254.99) and (869.14±280.26) N for the experimental and the control group, respectively, and no statistically significant differences were found between two groups (P〉O.05). Bevel fracture and horizontal fracture in the neck of root were the major fracture mode of the specimens. Under the circumstances of this study, it seems that cyclic loading does not affect the fracture strength and pattern of the quartz-fiber post-core-crown complex. To investigate whether masticatory fatigue affects the fracture resistance and pattern of lower premolars restored with quartz-fiber post-core and full crown, 44 single rooted lower premolars recently extracted from orthodontic patients were divided into two groups of 22 each. The crowns of all teeth were removed and endodontically treated and then restored with quartz-fiber post-core and full crown. Twenty-two teeth in one group were selected randomly and circularly loaded at 45° to the long axis of the teeth of 127.4 N at a 6 Hz frequency, and the other group was not delivered to cyclic loading and considered as control. Subsequently, all teeth in two groups were continually loaded to fail at 45° to the long axis of the teeth at a crosshead speed of 1 mm.min-1. The mean destructive force values were (733.88±254.99) and (869.14±280.26) N for the experimental and the control group, respectively, and no statistically significant differences were found between two groups (P〉O.05). Bevel fracture and horizontal fracture in the neck of root were the major fracture mode of the specimens. Under the circumstances of this study, it seems that cyclic loading does not affect the fracture strength and pattern of the quartz-fiber post-core-crown complex.
出处 《International Journal of Oral Science》 SCIE CAS CSCD 2012年第4期218-220,共3页 国际口腔科学杂志(英文版)
基金 supported by the Guangdong Province Science and Technology Commission (2008B080703019, 2011B080701010 and 2011B080701086)
关键词 fracture resistance masticatory fatigue pulpless teeth quartz-fiber fracture resistance masticatory fatigue pulpless teeth quartz-fiber
  • 相关文献

参考文献26

  • 1Sterzenbach G,Rosentritt M,Frankenberger R. Loading standardization of postendodontic restorations in vitro:impact of restorative stage,static loading,and dynamic loading[J].Operative Dentistry,2012,(01):71–79.
  • 2Bijelic J,Garoushi S,Vallittu PK. Fracture load of tooth restored with fiber post and experimental short fiber composite[J].Open Dent J,2011,(05):58–65.
  • 3Fokkinga WA,Kreulen CM,Le Bell-R(o)nnl(o) f Am. Fracture behavior of structurally compromised non-vital maxillary premolars restored using experimental fiber reinforced composite crowns[J].American Journal of Dentistry,2006,(06):326–332.
  • 4Kim YH,Lee JH. Influence of modification in core building procedure on fracture strength and failure patterns of premolars restored with fiber post and composite core[J].J Adv Prosthodont,2012,(01):37–42.
  • 5Naumann M,Metzdorf G,Fokkinga W. Influence of test parameters on in vitro fracture resistance of post-endodontic restorations:a structured review[J].Journal of Oral Rehabilitation,2009,(04):299–312.
  • 6Naumann M,Sterzenbach G,Pr(o)schel P. Evaluation of load testing of postendodontic restorations in vitro:linear compressive loading,gradual cycling loading and chewing simulation[J].Journal of Biomedical Materials Research Part B:Applied Biomaterials,2005,(02):829–834.
  • 7Albaladejo A,Osorio R,Aguilera FS. Effect of cyclic loading on bonding of fiber posts to root canal dentin[J].J BiomedMater Res B Appl Biomater,2008,(01):264–269.
  • 8Anderson DJ. Measurement of stress inmastication.I[J].Journal of Dental Research,1956,(05):664–670.
  • 9Hayashi M,Sugeta A,Takahashi Y. Static and fatigue fracture resistances of pulpless teeth restored with post–cores[J].Dental Materials,2008,(09):1178–1186.
  • 10Leong EW,Choon Tan KB,Nicholls JI. The effect of preparation height and luting agent on the resistance form of cemented cast crowns under load fatigue[J].Journal of Prosthetic Dentistry,2009,(03):155–164.

同被引文献48

引证文献10

二级引证文献89

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部