摘要
对 0 Cr1 3Ni4 Mo不锈钢在气蚀作用下的破坏形貌进行了微观分析。观察结果表明 ,其剥落形貌与冲击断口形貌相似 ,剥落机制主要是韧窝和准解理的混合型。
In this paper, the surface morphology of 0Cr13Ni4Mo stainless steel under cavitation attack was observed by scanning electron microcopy. The results showed that attaked surface had similar appearance like impact fractograph primary failure mechanism of cavitation damage was mixed mode of quasi cleavage and dimple fracture.
出处
《理化检验（物理分册）》
CAS
2000年第1期16-17,共2页
Physical Testing and Chemical Analysis(Part A:Physical Testing)