Vinyl acetate radical emulsion polymerization in water with GF51 silane co-monomer was performed by semi continuous way. The GF51 impacts on dispersion rheology as well on films and bonding strength properties were determined. It should be stated that even low quantities of GF51 （up to 6% from VAc） determined high viscosity of dispersions. The GF51 modified films have low water absorption and high affinity to glass. Molecular mass and thermal properties of GF51 modified polymers were determined accordingly.
Vinyl acetate radical emulsion polymerization in water with GF51 silane co-monomer was performed by semi continuous way. The GF51 impacts on dispersion rheology as well on films and bonding strength properties were determined. It should be stated that even low quantities of GF51 （up to 6% from VAc） determined high viscosity of dispersions. The GF51 modified films have low water absorption and high affinity to glass. Molecular mass and thermal properties of GF51 modified polymers were determined accordingly.