摘要
8wt%WO3/SiO2 metathesis （disproportionation） catalysts with different pore structures were prepared by the incipient-wetness-impregnation method. The as-synthesized catalysts were characterized by N2 adsorpfion-desorption, scanning electron microscopy （SEM）, X-ray diffraction （XRD）, UV-visible diffuse reflectance spectroscopy （DRS） and scanning transmission electron microscopy-high-angle annular dark field （STEM HAADF）. The results of STEM HAADF showed that WO3 species were not uniformly distributed on the SiO2 support. The experimental results of 8wt%WO3/SiO2 performance in ethene/decene metathesis revealed that the catalytic effect of 8wt%WO3/SiO2 catalyst and coke formation over it were closely related to the support pore structure： The 8wt%WO3/SiO2 catalyst with a more complicated pore structure showed better catalytic performance but the coke deposition rate was also faster.
8wt%WO3/SiO2 metathesis （disproportionation） catalysts with different pore structures were prepared by the incipient-wetness-impregnation method. The as-synthesized catalysts were characterized by N2 adsorpfion-desorption, scanning electron microscopy （SEM）, X-ray diffraction （XRD）, UV-visible diffuse reflectance spectroscopy （DRS） and scanning transmission electron microscopy-high-angle annular dark field （STEM HAADF）. The results of STEM HAADF showed that WO3 species were not uniformly distributed on the SiO2 support. The experimental results of 8wt%WO3/SiO2 performance in ethene/decene metathesis revealed that the catalytic effect of 8wt%WO3/SiO2 catalyst and coke formation over it were closely related to the support pore structure： The 8wt%WO3/SiO2 catalyst with a more complicated pore structure showed better catalytic performance but the coke deposition rate was also faster.