冲击接触载荷下45钢的微观塑性变形特征与损伤 被引量:6

CHARACTERISTICS OF MICRO-DEFORMATION AND DAMAGE OF MILD CARBON STEEL UNDER IMPACT CONTACT LOAD
下载PDF
导出
摘要 选取退火45钢为研究对象,考察冲击接触载荷下亚表层微观形变特征与损伤结果表明,冲击接触载荷下,铁素体的变形以多沿移为特征;滑移在品界受阻产生应力集中并产生力偶使晶粒发生相对转动,从而在品界产生裂纹; An examination of characteristics of micro-deformation and damage of mild carbon steel was conducted under impact contact load by SEM. The following results were obtained: (1) The characteristics of ferrite deformation under impact contact load is multi-slip; (2) Grain rotation which produces crack on the grain boundary was caused by force couple because slip is obstructed and stress concentrated on the grain boundary; (3) Sub-grain boundaries and sub-grains are the result of intersecting of different slip systems in different area within a ferrite grain.
出处 《金属学报》 SCIE EI CAS CSCD 北大核心 2000年第8期809-812,共4页 Acta Metallurgica Sinica
基金 国家自然科学基金资助项目!59771048
关键词 冲击接触载荷 微观形变特征 损伤 45钢 impact load, micro-characteristics of deformation, damage.
  • 相关文献

参考文献2

二级参考文献8

  • 1杨平生,张奇凤.冲击拉压疲劳试验机及试验方法[J].南昌大学学报(理科版),1994,18(1):41-48. 被引量:5
  • 2宋余九.金属的晶界与强度[M].西安:西安交通大学出版社,1988..
  • 3Yang P S,Mater Sci Eng A,1997年,234/236卷,127页
  • 4Yang P S,Fatigue,1994年,16卷,567页
  • 5杨平生,南昌大学学报.理科版,1994年,18卷,1期,41页
  • 6Liu W,Acta Metall Mater,1992年,40卷,763页
  • 7宋余九,金属的晶界与强度,1988年,93页
  • 8Lim L C,Acta Metall,1984年,32卷,1183页

共引文献9

同被引文献51

引证文献6

二级引证文献113

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部