烟囱用耐候钢在海水脱硫中的腐蚀研究及寿命预测 被引量:1

Corrosion Study and Life Prediction of Weathering Steel for Chimney in Seawater Desulfurization
下载PDF
导出
摘要 通过电化学技术、现场暴露试验研究了海水脱硫对电厂烟囱钢内衬Corten钢的腐蚀行为影响,并利用灰色模型GM(1,1)对烟囱内衬在实施海水脱硫工艺后的使用寿命进行了预测。研究结果表明,实施海水脱硫工艺后会加速烟囱内衬Corten钢的腐蚀且在烟囱140m高度附近腐蚀速率最大;Corten钢在腐蚀初期腐蚀速率逐渐增大,约1a后进入稳定腐蚀状态;Corten钢焊缝区相对于基体是阴极,处于被保护状态;Corten钢在海水脱硫烟气中最大腐蚀速率的灰色预测公式为x(k+1)=-0.43211e-0.10515k+0.45811。 The influence of seawater desulfurization on the corrosion behavior of Corten steel-weathering steel for chimney was studied based on electrochemical techniques and field exposure test. The service life of chimney lining was forecasted after implementing seawater desulfurization to the chimney lining by using grey model GM( 1,1 ). The result showed that the implement of seawater desulfurization accelerates the corrosion of Corten steel for chimney lining and the corrosion rate reaches maximum at 140-meter high place of the chimney; the corrosion rate of Corten steel increases gradually at the initial stage and the corrosion rate of Corten steel becomes stable about 1 year later; the weld area of Corten steel is cathode relative to the base and in a protected status; in the fuel gas of seawater desulfurization, the grey forecast formula of maximal corrosion rate of Corten steel is x(k+1)=-0.43211e-0.10515k+0.45811.
出处 《装备环境工程》 CAS 2013年第1期17-21,40,共6页 Equipment Environmental Engineering
关键词 海水脱硫 Corten钢 灰色模型 腐蚀行为 seawater desulfurization Corten steel grey model corrosion behavior
  • 相关文献

参考文献6

二级参考文献4

共引文献357

同被引文献19

  • 1植田昌克.合金元素和显微结构对CO_2/H_2S环境中腐蚀产物稳定性的影响[J].石油与天然气化工,2005,34(1):43-52. 被引量:34
  • 2齐慧滨,刘海平,何业东,朱日彰,北京腐蚀与防护中心冶金部腐蚀-磨蚀与表面技术开放实验室.金属高温硫化研究进展[J].腐蚀科学与防护技术,1996,8(2):114-121. 被引量:10
  • 3MROWEC S, HASHIMOTO K. Chemical Diffusion in Non- stoic, hiometric Metal Sulphides [ J 1. Journal of Material Sci- ence, 1995,30:4801---4816.
  • 4MROWEC S, PRZYBYLSKI K. Transport Properties of Sul- fide Scales and Sulfidation of Metals and Alloys [ J ]. Oxida- tion of Metals, 1985,23 : 107--139.
  • 5MROWEC S, WALEC T, WERBER T. High-temperature Sul- fur Corrosion of Iron-Chromium Alloys [ J ]. Oxidation of Me- tals, 1969,1 ( 1 ) :93--120.
  • 6YUAN Shao-jun. Surface Chemistry and Corrosion Behaviour of 304 Stainless Steel in Simulated Seawater Containing In- organic Sulphide and Sulphate-reducing Bacteria[ J]. Corro- sion Science, 2013,74 : 353--366.
  • 7HERBERT J. Surface Chemistry and Morphology of Poorly Crystalline Iron Sulfides Precipitated in Media Containing Sulfate-reducing Bacteria [ J ]. Chemical Geology, 1998, 144:87--97.
  • 8TECHKARNJANARUK S. Iron Sulfides and Sulfur Species Produced at Hematite Surfaces in the Presence of Sulfate- reducing Bacteria [ J 1- Geoehimiea Cosmochimiea Acta, 2001,65 ( 2 ) : 223--235.
  • 9YAGI H. Chemical Diffusion and Electrical Conductivity of Ni3x S2 [ J ]. Oxidation of Metals, 1982,18 ( 1/2 ) :41--53.
  • 10LEE T W. Sulfidation Behavior of Inconel 738 Superalloy at 500 - 900 C [ J ] Oxidation of Metals, 2001,56 (1/2) : 51--71.

引证文献1

二级引证文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部