摘要
To improve the oxidation resistance of carbon/carbon （C/C） composites, mullite coating was prepared on the surface of SiC-coated C/C composites by supersonic plasma spraying. Phases and microstructures of mullite coating were characterized by X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The coating primarily consists of a single phase of mullite （3AI203-2SIO2）. The SEM results show that mullite coating was continuous and well bonded with the SiC inner layer without penetrating crack. Mullite coating exhibited good oxidation resistance, After 98.5 h oxidation at 1773 K and 9 thermal shock cycles between 1773 K and room temperature, the weight loss of the coated C/C composites was only 2.57%.
To improve the oxidation resistance of carbon/carbon （C/C） composites, mullite coating was prepared on the surface of SiC-coated C/C composites by supersonic plasma spraying. Phases and microstructures of mullite coating were characterized by X-ray diffraction （XRD） and scanning electron microscopy （SEM）. The coating primarily consists of a single phase of mullite （3AI203-2SIO2）. The SEM results show that mullite coating was continuous and well bonded with the SiC inner layer without penetrating crack. Mullite coating exhibited good oxidation resistance, After 98.5 h oxidation at 1773 K and 9 thermal shock cycles between 1773 K and room temperature, the weight loss of the coated C/C composites was only 2.57%.
基金
supported by the National Natural Science Foundation of China under Grant No. 51072166 and No.50902111
the "111" Project under Grant No.D08040
NPU Foundation for Fundamental Research and the Research Fund of the State Key Laboratory of Solidification Processing(NWPU), China (Grant No.73-QP-2010)