摘要
The efficient Eu2＋ -doped Ba3 Si6O12N2 green phosphors were prepared by a traditional solid state reaction method under N2 /H2 atmosphere at a temperature up to 1350 ℃ for 12h. Photoluminescence （PL） properties showed a broad emission band with a peak of 525 nm and the full width of half-emission maximums （FWHM） of 70 nm under 460 nm light irradiation. The X-ray diffraction patterns （XRD） and scanning electron microscope （SEM） images of the synthesized powder demonstrated its pure phase and excellent crystallization. Quenching concentration in this phosphor was found to be 0.3. The mechanisms of concentration quenching and redshift of emission peak with increasing concentration of Eu2＋ were studied. The temperature dependence measurement of this green phosphor revealed excellent thermal quenching property compared to silicate green phosphor. It is believed that Ba3 Si6O12N2 ：Eu2＋ is an excellent green phosphor for UV or blue chip based white LEDs.
The efficient Eu2＋ -doped Ba3 Si6O12N2 green phosphors were prepared by a traditional solid state reaction method under N2 /H2 atmosphere at a temperature up to 1350 ℃ for 12h. Photoluminescence （PL） properties showed a broad emission band with a peak of 525 nm and the full width of half-emission maximums （FWHM） of 70 nm under 460 nm light irradiation. The X-ray diffraction patterns （XRD） and scanning electron microscope （SEM） images of the synthesized powder demonstrated its pure phase and excellent crystallization. Quenching concentration in this phosphor was found to be 0.3. The mechanisms of concentration quenching and redshift of emission peak with increasing concentration of Eu2＋ were studied. The temperature dependence measurement of this green phosphor revealed excellent thermal quenching property compared to silicate green phosphor. It is believed that Ba3 Si6O12N2 ：Eu2＋ is an excellent green phosphor for UV or blue chip based white LEDs.
基金
Project supported by National Natural Science Foundation of China(51102021)
the Natural Science Foundation of Beijing(2102022)
the National High Technology Research and Development Program of China(2010AA03A404,2011AA03A101)