摘要
TiC/TisSi3 composites were fabricated on Ti-5A1-2.5Sn substrates by gas tungsten arc welding （GTAW）. Identification of the phases was performed using X-ray diffraction （XRD）. The microstructures were analyzed using scanning electron microscopy （SEM） combined with energy-dispersive X-ray spectrometry （EDS） and optical microscopy （OM）. The Vickers hardness was measured with a micro-hardness tester. The TiC/TisSi3 composites were obtained in a double-layer track, and the Vickers hardness of the track increased by two to three times compared with the Ti-5A1-2.5Sn substrate.
TiC/TisSi3 composites were fabricated on Ti-5A1-2.5Sn substrates by gas tungsten arc welding （GTAW）. Identification of the phases was performed using X-ray diffraction （XRD）. The microstructures were analyzed using scanning electron microscopy （SEM） combined with energy-dispersive X-ray spectrometry （EDS） and optical microscopy （OM）. The Vickers hardness was measured with a micro-hardness tester. The TiC/TisSi3 composites were obtained in a double-layer track, and the Vickers hardness of the track increased by two to three times compared with the Ti-5A1-2.5Sn substrate.
基金
financially supported by the Foundation of Education Department of Guangdong Province,China (No. 2010A090200034)