TiCN/VCN多层膜的力学和摩擦磨损性能 被引量:8

Mechanical and tribological performances of TiCN/VCN multilayer films
下载PDF
导出
摘要 采用多靶磁控溅射技术,制备TiCN、VCN单层膜及一系列调制比为1的不同调制周期的TiCN/VCN多层膜。利用X射线衍射仪、纳米压痕仪、高温摩擦磨损测试仪和扫描电子显微镜,研究各种薄膜的微结构、力学性能及室温和高温摩擦磨损性能。研究表明:不同调制周期的TiCN/VCN多层膜的硬度围绕混合法则计算的硬度值上下波动,没有出现致硬现象。TiCN和VCN单层薄膜室温下的摩擦因数很低,TiCN/VCN多层膜调制周期较小时摩擦因数较高,调制周期大于10 nm时摩擦因数逐渐接近TiCN和VCN单层膜。700℃下,TiCN/VCN多层膜的摩擦因数主要取决于表面生成的TiO2和V2O5的共同作用,与TiCN相比,TiCN/VCN多层膜的高温摩擦因数较小。 TiCN, VCN monolithic films and TiCN/VCN mutilayers with different modulation periods were prepared by multi-target magnetic sputtering. The microstructure, mechanical properties, friction and wear properties at room and high-temperature of films were characterized by X-ray diffraction, nano-indentation, and CSM high-temperature ball-on-disc tribometer. The results show that the hardness of TiCN/VCN multilayers is close to the value calculated around the rule of mixtures, and super high hardness does not appear. The friction coefficients of TiCN and VCN films arc very low in room-temperature. The friction coefficients of TiCN/VCN mutilayers are higher when their modulation periods are small, but when their modulation periods are more than 10nm, the friction coefficients of TiCN/VCN mutilayers will he close to that of the TiCN and VCN films. When the temperature reach to 700℃, The friction coefficients of TiCN/VCN mutilayers are depending on TiO2 and V205. Compared with TiCN films, the friction coefficient of TiCN/VCN mutilayers decrease at high temperature.
出处 《粉末冶金材料科学与工程》 EI 北大核心 2013年第1期132-138,共7页 Materials Science and Engineering of Powder Metallurgy
基金 国家自然科学基金资助项目(51074080) 江苏省自然科学基金资助项目(BK2008240) 江苏省研究生科研创新计划(CXLX11_0292)
关键词 TICN VCN 磁控溅射 力学性能 摩擦磨损性能 TiN/VCN magnetron sputtering mechanical properties friction properties
  • 相关文献

参考文献3

二级参考文献30

  • 1唐达培,高庆,江晓禹.氮碳化钛涂层的结构性能及结合强度[J].表面技术,2004,33(4):13-15. 被引量:6
  • 2魏莎莎,钟启茂.TiAIN涂层与TiCN涂层硬质合金刀具性能对比[J].机械制造,2006,44(12):48-49. 被引量:9
  • 3严永林,郑勇,于海军,卜海建.氮碳化钛涂层制备技术的研究进展[J].材料导报,2007,21(7):55-58. 被引量:3
  • 4Kiryukhantsev-Korneev Ph V, Shtansky D V, Petrzhik M I, et al. Thermal stability and oxidation resistance of Ti-B-N, Ti-Cr-B-N, Ti-Si-B-N and Ti-Al-Si-B-N films[ J]. Surface and Coatings Technology, 2007, 201 ( 13 ) :6143 - 6147.
  • 5Jiang Ning, Shen Y G, Zhang H J, et al. Superhard nanocomposite Ti-A1-Si-N films deposited by reactive unbalanced magnetron sputtering[ J]. Materials Science and Engineering B, 2006, 135( 1 ) :1 -9.
  • 6Li Chen, Wang S Q, Zhou S Z, et al. Microstructure and mechanical properties of Ti ( C, N) and TiN/Ti ( C, N) multilayer PVD coatings [ J ]. International Journal of Refractory Metals and Hard Materials, 2008, 25 (5) :456 - 460.
  • 7Yang J H, Chen K H, Wang S Q, et al. Characteristics and performance of Ti( C, N) coatings synthesized by magnetron sputtering technique[ J]. J Alloys and Compd,2008,471 ( 1 - 2 ) : 162 - 165.
  • 8Leparoux M, Kihn Y, Paris S, et al. Microstructure analysis of RF plasma synthesized TiCN nanopowders[ J]. International Journal of Refractory Metals & Hard Materials, 2008, 26 (4) :277 - 285.
  • 9Tavares C J, Rebouta L, Almeida B, et al. Structural characterization of muhilayered sputtered TiN/ZrN coatings [J]. Surface and Coatings Technology, 1998, 100- 101:65-71.
  • 10YU Li-hua, DONG Shi-run, XU Jun-hua, et al. Microstructure and hardening mechanisms in a-Si3N4/nc-TiN nanostructured multilayers[ J]. Thin Solid Films, 2008, 516 (8) :1864 - 1870.

共引文献49

同被引文献119

引证文献8

二级引证文献80

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部