二环[2.2.1]庚烷二羧酸盐成核剂对聚丙烯结晶行为和力学性能的影响 被引量:7

Effects of Nucleating Agent Bicyclicheptane Di-carboxylate on Crystallization Behaviors and Mechanical Properties of Polypropylene
下载PDF
导出
摘要 研究了二环[2.2.1]庚烷二羧酸盐成核剂(商品名:HPN-68)对聚丙烯(PP)结晶行为和力学性能的影响。结果表明:HPN-68是一种典型的聚丙烯α晶型成核剂,在PP中具有很高的成核效率。在较低的添加浓度下可明显提高PP的结晶峰温度和力学性能。然而,其添加量存在一个饱和值。当成核剂含量达到该饱和值以后,PP的结晶峰温度和力学性能就趋于稳定。当成核剂HPN-68的添加量为0.2 phr时,PP的结晶峰温度可升高15℃左右,拉伸强度和弯曲模量分别可提高12.7%和18.2%。 Effects of bicyclic [ 2, 2, 1 ] heptane di-carboxylate ( commercial product name : HPN-68 ) on the crystallization behaviors and mechanical properties of polypropylene (PP) were studied in this paper. The results showed that HPN-68 was a typical nucleating agent for a-PP and it had high nucleation efficiency in PP. Crystallization peak temperature and mechanical properties of PP nucleated with HPN-68 can be greatly increased under low concentration of HPN-68. However, the addition concentration of nucleating agent HPN-68 had a saturation value and properties of PP will tend to stable after concentration of HPN-68 exceeded the saturation value. When the addition concentration of HPN-68 was 0.2 phr, the crystallization peak temperature can be increased by about 15C, and the tensile strength and flexural modulus of PP can he increased by 12.7% and 18.2%, respectively.
出处 《塑料工业》 CAS CSCD 北大核心 2013年第3期76-78,共3页 China Plastics Industry
基金 湖南省教育厅资助科研项目(10B004) 湖南省科技计划项目(2012FJ3002 2009GK3015) 长沙理工大学大学生创新实验项目 国家自然科学基金项目(21202010) 湖南省自然科学基金青年项目(12JJ4021)
关键词 聚丙烯 成核剂 结晶行为 力学性能 PP Nucleating agent Crystallization Behaviors Mechanical properties
  • 相关文献

参考文献8

二级参考文献74

共引文献116

同被引文献57

  • 1李馥梅.透明聚丙烯的制备方法及性能控制因素[J].塑料科技,2004,32(5):39-45. 被引量:13
  • 2张丽英,武志军,张浩.成核剂对聚丙烯结晶形态及力学性能的影响[J].合成树脂及塑料,2004,21(4):46-49. 被引量:19
  • 3邱慎海,包宗宏.共沸物进料裂解双环戊二烯实验研究[J].石油学报(石油加工),2006,22(4):25-29. 被引量:8
  • 4全国塑料标准化技术委员会.塑料弯曲性能的测定:GB/T9341-2008[S].北京:中国标准出版社,2008.
  • 5KUMAR R, DHALIWAI. J S, KAPURGS, etal. Mechan- ical properties of modified biofiller-polyproll)ylene composites [J]. Polymer Composites. 201.1, 35(4): 708- 714.
  • 6SAI.AS-PAPAANOPOLOS H, MORAI.ES A B. LOANO T, et a[. Improvement of toughness properties of polypropyl- ene/wollastonite composites using an interface modifier[J]. Polymer Composites, 2013, 10(3): 1184 -1192.
  • 7GRANLUND H, ANDREASSEN E, SKJONSFJEIA. E, et al. Measuring and simulating morphology gradients in injec tion molded talc-reinforced isotactic polypropylene[J]. Jour nal of Polymer Science Part P,: Polymer Physics, 2014, 52 (]7): 1157-1167.
  • 8LIBSTER I), ASERIN A, GART1 N. Advanced nucleating agents for poiypropylene[J]. Polymers for Advanced Teeh nologies, 2007, 18(9) : 685-695.
  • 9FANEGAS N, GOMEZ M A, MARCO C. et al. Influence of a nucleating agent on the crystallization behaviour of lsotactic polypropylene and elastomer blends[J]. Polymer. 2007, 48 (18) : 5324-5331.
  • 10LONG I. J, HE W T, ZHANG M M. et al. Nucleation effects of sodium and ammonium salts of 2, 2'-methylene-bis- (4, 6-di-t-butylphenylene) phosphate in isotactic polypropyl- ene[J]. Polymer Engineering &. Science, 2015. 55( 1 ) : 22- 28.

引证文献7

二级引证文献25

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部