主要对航天用硅橡胶制品的贮存试验研究进展情况进行了梳理总结,在此基础上指出目前存在以下三方面不足:自然贮存试验开展得少而且数据没有充分挖掘、利用;单应力加速老化试验开展得多,综合应力加速试验开展得少;贮存试验中对产品宏观性能变化关注得多,对其微观结构变化和老化机理研究得少。针对这些问题,指出了今后应在自然贮存试验信息的积累和应用、综合应力贮存试验和贮存老化机理等方面加强研究。
Research progress on storage aging tests of silicone rubber for spaceflight application was reviewed and analyzed in this paper. There are three problems in the present storage aging researches. Firstly, accelerated ag-ing tests (be abbreviated to AAT) were largely conducted but natural aging tests (be abbreviated to AAT) were con-ducted much fewer. Secondly, AAT with a single accelerated stress was largely conducted but AAT with multi accel-erated stress was conducted much fewer. Finally, the variations of macroscopical performances had attracted too much attention but the aging mechanism and variations of microcosmic structures were concerned too little. Based on the problems mentioned above, three research fields including data accumulation in AAT and its applications, AAT with multi accelerated stress and aging mechanism of silicone rubber should be emphasized in the future researches.
出处
《宇航材料工艺》
CAS
CSCD
北大核心
2013年第1期26-29,共4页
Aerospace Materials & Technology
关键词
硅橡胶
贮存试验
研究进展
Silicone rubber, Aging test, Research progress