摘要
Ag-based brazing foils, BAg-8 （72Ag-28Cu in wt%） and Ticusil （68.8Ag-26.7Cu-4.5Ti in wt%） were selected to braze Zr. Interfacial AgCu4Zr, CuZr2 reaction layers and Ag-rich matrix dominate BAg-8 brazed joint, and fractograph after shear test shows ductile dimple fracture with plastic sliding marks. Ticusil joint brazed at 910℃ for 300 s is comprised of CugZr11 and AgZr intermetallics, and fractograph after shear test displays brittle cleavage fracture.
Ag-based brazing foils, BAg-8 （72Ag-28Cu in wt%） and Ticusil （68.8Ag-26.7Cu-4.5Ti in wt%） were selected to braze Zr. Interfacial AgCu4Zr, CuZr2 reaction layers and Ag-rich matrix dominate BAg-8 brazed joint, and fractograph after shear test shows ductile dimple fracture with plastic sliding marks. Ticusil joint brazed at 910℃ for 300 s is comprised of CugZr11 and AgZr intermetallics, and fractograph after shear test displays brittle cleavage fracture.