以胶凝用量、细料含量、水胶比作为胶凝砂砾石材料抗压强度的影响因素,通过正交试验设计配合比,采用极差法和投影寻踪回归分析(PPR)两种方法分析试验结果,得到了影响胶凝砂石材料抗压强度影响因素的主次顺序为胶凝用量、水胶比、细料含量;胶凝砂砾石材料的抗压强度在各因素不同水平下的变化规律,即抗压强度随胶凝用量的增加而增大,最佳水胶比为1.2,细料含量在25%~30%之间时抗压强度达到最大,当水胶比和细料含量继续变大时,抗压强度有所降低。
Gelling the amount of the fines content,water glue than the compressive strength of sand and gravel as a gelling material impact factors, mixing ratio by orthogonal experimental design,the range analysis and projection pursuit regression (PPR) were two ways to analyze the test results, the order was affected gelling compressive strength of the sand and gravel material impact factors gelling amount of a water-cement ratio, the fines content.The variation of the compressive strength of the gelling sand and gravel materials in the different levels of each factor, that the compressive strength increased with increasing gelling amount of optimum water-cement ratio of 1.2 the fines content reached the maximum compressive strength of between 25% to 30%, when the water-cement ratio and the fines content continue to change was large, the compressive strength decreased.
出处
《混凝土》
CAS
CSCD
北大核心
2013年第3期77-80,共4页
Concrete
基金
新疆水利水电重点学科基金(XJXZ-2003-16)
关键词
胶凝砂砾石
抗压强度
胶凝用量
水胶比
细料含量
gement sand and gravel
compressive strength
amount of gel
water-binder ratio
fine content