通过固相法合成掺铈榍石固溶体(Ca0.9Ce0.1Ti0.8Al0.2SiO5),采用PCT粉末浸泡试验法,借助X射线衍射(XRD)、扫描电镜(SEM)、电感耦合等离子体发射光谱(ICP-OES)等分析测试手段,研究掺铈榍石固溶体在热液作用下的稳定性。实验结果表明,掺铈榍石固化体在不同条件下(温度150~200℃,0.476~1.554 MPa,pH值5~9),都具有良好的稳定性。随着浸泡时间的增加,各元素的归一化浸出率逐渐降低并保持在较低水平。
The sphene doped cerium(Ca 0.9 Ce 0.1 Ti 0.8 Al 0.2 SiO 5) was synthesized by solid-reaction.The chemical durability was investigated with a long-term product consistency test(PCT) by X-ray diffraction(XRD),scanning electron microscopy(SEM),and inductively coupled plasma atomic emission spectrometry(ICP-OES).The results indicated that the synthesized sphene has good chemical durability under coupling effect of hydrothermal conditions of 150 ~ 200℃,0.476 ~ 1.554 MPa,and 5 ~ 9 pH.With the increase of soaking time,the normalized leaching rate of elements gradually decreases and maintaines at a lower level.
出处
《四川大学学报(工程科学版)》
EI
CAS
CSCD
北大核心
2013年第2期162-166,共5页
Journal of Sichuan University (Engineering Science Edition)
基金
国家自然科学基金资助项目(10775113)
四川省教育厅资助科研项目(10ZB013)
西南科技大学四川省非金属复合与功能材料重点实验室开放基金资助项目(10zxfk07)
关键词
榍石固溶体
浸出率
稳定性
铈
sphene solid solution
leaching rate
chemical durability
cerium