As a kind of low-cost and readily available industrial byproduct, ethylene tar （ET） was for the first time utilized for the preparation of heat-resistant condensed polynuclear aromatic resin （COPNAR）. The basic properties of ET and the resulted COPNAR were characterized by FT-IR, IH-NMR, TGA and elemental analysis. The test results showed that ET with high aromatic content （〉50%） was suitable for the synthesis of COPNAR with superior heat resistance. The average molecular structure of ET was obtained by means of the improved Brown-Ladner method, and the reaction mechanism was considered as an acid-catalyzed positive ion-typed polymerization. Our findings have provided a new route to develop ET into technology-added heat-resistant resins.
As a kind of low-cost and readily available industrial byproduct, ethylene tar (ET) was for the first time utilized for the preparation of heat-resistant condensed polynuclear aromatic resin (COPNAR). The basic properties of ET and the resulted COPNAR were characterized by FT-IR, 1H-NMR, TGA and elemental analysis. The test results showed that ET with high aromatic content (>50%) was suitable for the synthesis of COPNAR with superior heat resistance. The average molecular structure of ET was obtained by means of the improved Brown-Ladner method, and the reaction mechanism was considered as an acid-catalyzed positive ion-typed polymerization. Our findings have provided a new route to develop ET into technology-added heat-resistant resins.
基金
supported by the Program for New Century Excellent Talents in University, China Ministry of Education, 2009 (No. NCET-10-0768)
the National Natural Science Foundation of China (Nos. 20876176 and 51172285)
the Natural Science Foundation of Shandong Province (ZR2011EL031, ZR2011EL030)