铕掺杂硫酸氧钆红色荧光粉的制备及发光性能 被引量:3

Preparation and Luminous Property of Ga_(2-x)O_2SO_4:xEu^(3+) Red Phosphors
下载PDF
导出
摘要 采用共结晶-高温煅烧法和共混合-高温煅烧法合成了Gd2-xO2SO4:xEu3+系列荧光粉,用XRD、SEM和荧光光谱分析技术对样品的晶体结构、表面形貌及发光性能进行表征。结果表明:两种方法在950℃合成的Gd2-xO2SO4:xEu3+系列荧光粉都具有单一物相,在紫外波长激发下都发出618 nm红光。然而,发光强度和粒子特性存在差异,共结晶-高温煅烧法比共混合-高温煅烧法合成的样品显示出更强的红光和较好的粒子形貌。最佳的铕掺杂量x=0.10,最佳煅烧温度为950℃。荧光粉的粒度在500 nm左右。 A series of fluorescent powders of Gd2-xO2SO4:xEu3+ have been synthesized by two methods: the co-crystallization followed by calcinations (CCC) method and the co-mixture followed by calcinations (CMC) method. The as-prepared phosphors were examined by means of X-ray dif- fraction (XRD), scanning electron spectroscopy (SEM) and photoluminescence spectrometer (PLS). The results show that Gd2-xO2SO4:xEu3+ phosphors with single crystalline phase have been successfully prepared with both methods at calcinations temperature around 950 ℃, and emit red light at 618 nm under ultraviolet exitation. However, the emission strength and particle characteriza- tion are different. It is proved that the phosphors prepared by CCC method have stronger red emis- sion and better morphogy of the particles than that by CMC method. The optimal Eu doping content and calcinations temperature are determined to be x = 0.1 and 950 ℃. The particle size of as-syn- thesized phosphors is around 500 nm.
机构地区 南昌大学化学系
出处 《发光学报》 EI CAS CSCD 北大核心 2013年第4期411-415,共5页 Chinese Journal of Luminescence
基金 科技部863课题(2010AA03A400) 科技部973课题(2012CBA01204) 国家自然科学基金(21261014 51274123) 江西省主要学术带头人资助计划(2007DD00800)资助项目
关键词 硫酸氧钆 共结晶 荧光粉 制备 gadolinium oxide sulfate co-crystallization phosphor preparation
  • 相关文献

参考文献4

二级参考文献34

  • 1XIE An, YUAN XiMing, WANG JuanJuan & WANG Feng Engineering Research Center of Nano-Mineral Materials and Application, Ministry of Education, Faculty of Materials Science and Chemical Engineering, China University of Geosciences, Wuhan 430074, China.Synthesis and photoluminescence property of red phosphors LiEu_(1-x)Y_x(WO_4)_(0.5)(MoO_4)_(1.5) for white LED[J].Science China(Technological Sciences),2009,52(7):1913-1918. 被引量:7
  • 2廖勇,朱伟,黎学明,莫芸绮,郝小光,马小强.溶胶-凝胶法制备Li(MoO_4)_2∶Eu及表征[J].材料导报,2007,21(F05):321-324. 被引量:14
  • 3刘行仁.白光LED固态照明光转换荧光体[J].发光学报,2007,28(3):291-301. 被引量:75
  • 4张思远.稀土离子的光谱学[M].北京:科学出版社,2008.
  • 5Ekambaram S, Patil K C, Maaza M. Synthesis of lamp phos- phors: facile combustion approach [ J ]. J. Alloys Compd. , 2005, 393(1-2) : 81.
  • 6Bass M. Electrooptic Q switching of the Nd:YVO4 laser without an intracavity polarizer [ J], IEEE J. Quantum Electron. , 1975, 11 : 938.
  • 7O'Connor J R. Unusual crystal-field energy levels and efficient laser properties of Nd: YVO4[J]. Appl. Phys. Lett., 1966, 9 (ll): 407.
  • 8Fields R A, Birnbaum M, Fincher C L. Highly efficiency Nd: YVO4 diode-laser end-pumped laser [ J]. Appl. Phys. Lett. , 1987, 51(23) : 1885.
  • 9Levine A K, Palilla F C. A new highly efficient red-emitting eathod luminesent phosphor ( YVO4 : Eu ) for coLor television [J].Appl. Phys. Lett., 1964, 5(6) : 118.
  • 10Gemer P, Kramer K, Gudel H U. Broad-band Cr^5+-sensitizedEr^3+ luminescence in YVO4[J]. J. Lumin. , 2003, 102: 112.

共引文献61

同被引文献49

  • 1Machida M, KawanoT, Eto M, et al. Ln dependence of the large-capacity oxygen storage/release property of Ln oxysulfate/oxysulfide systems[ J]. Chem. Mater. ,2007,19(4) :954-960.
  • 2Machida M, Kawamura K, Ito K,et al. Large-capacity oxygen storage by lanthanide oxysulfate/oxysulfide systems [ J ]. Chem. Mater. ,2005,17 (6) 1487-1492.
  • 3Zhang D, Yoshioka F, Ikeue K, et al. Synthesis and oxygen release/storage properties of Ce-substituted La-oxysulfates, ( La1-x Ce, ) 2 O2 SO4 [ J ]. Chem. Mater. ,2008,20:6697-6703.
  • 4Paul W. Magnetism and magnetic phase diagram of Gd2 02 S04-1 experiments[ J ]. J. Magn. Magn. Mater. , 1990,87:23-28.
  • 5Kratz W, Kahle H G, Paul W. An ac method for measuring the specific heat of small probes and an application in the study on Gd: O2 SO4 [ J ]. J. Magn. Magn. Mater. , 1996,161:249-254.
  • 6Porcher P, Svoronos D R. Preparation and optical properties of europium-activated rare earth oxysulfates [ J]. J. Solid State Chem. 1983,46: 101- 111.
  • 7Kijima T, Shinbori T, Sekita M, et al. Abnormally enhanced Eu3 + emission in Y202SO4:Eu3 + inherited from their precursory dodecylsulfate- templated concentric -layered nanostrueture [ J ]. J. Lumin. ,2008,128 ( 3 ) : 311-316.
  • 8Tomaszewicz E, Leniee G, Kaczmarek S M. Re-investigations of thermal decomposition of gadolinium sulfate oetahydrate [ J ]. J. Therm. Anal. Calorim, 2010,102 : 875 -881.
  • 9Ikeue K, Kawano T, Eto M, et al. X-ray structural study on the different redox behavior of La and Pr oxysulfates/oxysulfides [ J ]. J. Alloy. Compd. , 2008,451 (1-2) :338-340.
  • 10Liang J B, Ma R Z, Geng F X, etal. Ln2 (OH) 4 SO4 · nil20 ( Ln = Pr to Tb ; n - 2) : A new family of layered rare-earth hydroxides rigidly pillared by sulfate inns[ J ]. Chem. Mater. ,2010,22:6001-6007.

引证文献3

二级引证文献2

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部