摘要
用粉煤灰中提取的空心微珠对无机硅酸锌涂层进行改性,通过电化学测试和盐雾试验对比研究无机硅酸锌涂层改性前后的耐腐蚀性能,并利用扫描电镜观察涂层的微观结构。结果表明:经预处理后的空心微珠改善了涂层的耐腐蚀性能,空心微珠的加入显著提高了涂层的致密度。此外,在腐蚀过程中生成的腐蚀产物与涂层微孔结构结合良好,有效提高了腐蚀介质向涂层内部渗透的阻力,对基体起到了良好的保护作用。
Inorganic zinc-silicate coatings were modified by cenospheres extracted from fly ash. The corrosion resistance of the coatings before and after modification was contrasted by electrochemical tests and salt spray test. The microstructure of the coatings was observed by scanning electron microscope (SEM). The results showed that the corrosion resistance of the coatings could be improved by adding the preprocessed cenosph- eres. The density of zinc-silicate coatings was obviously improved by adding cenospheres. In addition, the cor- rosion products generated in the corrosion process combined were well with the micro-porous coatings' structure, which increased the resistance of corrosive medium permeating into the coatings effectively, and then effectively protected the substrate.
出处
《中国表面工程》
EI
CAS
CSCD
北大核心
2013年第2期87-91,共5页
China Surface Engineering
关键词
空心微珠
无机硅酸锌
电化学阻抗
盐雾试验
腐蚀性能
cenospheres
inorganic zinc-silicate coating
electrochemical impedance spectroscopy
salt spray test
corrosion resistance