The linear elasticity was studied in a martens- tic alloy NisoMn25Ga9Cu16. A 0.4 % linear elastic strain is btained in the polycrystalline sample under compressive stress of 745 MPa. The elastic modulus is 186 GPa. The obtained linear elastic strain and elastic modulus are much higher than that of ternary Ni-Mn-Ga martensitic alloys.~.bstract The linear elasticity was studied in a martens- tic alloy NisoMn25Ga9Cu16. A 0.4 % linear elastic strain is ~btained in the polycrystalline sample under compressive stress of 745 MPa. The elastic modulus is 186 GPa. The obtained linear elastic strain and elastic modulus are much higher than that of ternary Ni-Mn-Ga martensitic alloys.
The linear elasticity was studied in a martens- tic alloy NisoMn25Ga9Cu16. A 0.4 % linear elastic strain is btained in the polycrystalline sample under compressive stress of 745 MPa. The elastic modulus is 186 GPa. The obtained linear elastic strain and elastic modulus are much higher than that of ternary Ni-Mn-Ga martensitic alloys.~.bstract The linear elasticity was studied in a martens- tic alloy NisoMn25Ga9Cu16. A 0.4 % linear elastic strain is ~btained in the polycrystalline sample under compressive stress of 745 MPa. The elastic modulus is 186 GPa. The obtained linear elastic strain and elastic modulus are much higher than that of ternary Ni-Mn-Ga martensitic alloys.
基金
financially supported by the National Basic Research Program of China (973 Program) under grant 2012CB619404
the National Natural Science Foundations of China(Nos. 50925101,51221163, and 51001004)
the National Basic Research Program of China (No. 2012CB619404)