Crystallographic Analysis of Isothermally Transformed Bainite in 0.2C-2.0Mn-1.5Si-0.6Cr Steel Using EBSD 被引量:3

Crystallographic Analysis of Isothermally Transformed Bainite in 0.2C-2.0Mn-1.5Si-0.6Cr Steel Using EBSD
原文传递
导出
摘要 The crystallography of bainite, transformed isothermally at 450 ℃ in 0.2C-2.0Mn-1.5Si-0.6Cr steel, was investigated by electron backscatter diffraction (EBSD) analysis. The orientation relationship (OR) was found to be closer to Nishiyama-Wassermann (N-W) than Kurdjumov-Sachs orientation relationship. Bainite microstructure consisted of parallel laths forming a morphological packet structure. Typically, there were three different lath orientations in a morphological packet. These orientations were dictated by a three specific N-W OR variants sharing the same {111} austenite plane. A packet of bainite laths with common {111} austenite plane was termed as crystallographic packet. Generally, the crystallographic packet size corresponded to the morphological packet size. Locally, crystallographic packets with only two dominant orientations were observed. This indicates strong local variant selection during isothermal bainite transformation. The relative orientation between the variants in crystallographic packets was found to be near 60°/〈110〉. This appears to explain the strong peak observed in the grain boundary misorientation distribution near 60°. Bainite also contained pronounced fraction of boundaries with their misorientation in the range of 2.5°-8° with quite widely dispersed rotation angles. Spatially these boundaries were found to locate inside the bainite laths, forming lath-like sub-grains. The crystallography of bainite, transformed isothermally at 450 ℃ in 0.2C-2.0Mn-1.5Si-0.6Cr steel, was investigated by electron backscatter diffraction (EBSD) analysis. The orientation relationship (OR) was found to be closer to Nishiyama-Wassermann (N-W) than Kurdjumov-Sachs orientation relationship. Bainite microstructure consisted of parallel laths forming a morphological packet structure. Typically, there were three different lath orientations in a morphological packet. These orientations were dictated by a three specific N-W OR variants sharing the same {111} austenite plane. A packet of bainite laths with common {111} austenite plane was termed as crystallographic packet. Generally, the crystallographic packet size corresponded to the morphological packet size. Locally, crystallographic packets with only two dominant orientations were observed. This indicates strong local variant selection during isothermal bainite transformation. The relative orientation between the variants in crystallographic packets was found to be near 60°/〈110〉. This appears to explain the strong peak observed in the grain boundary misorientation distribution near 60°. Bainite also contained pronounced fraction of boundaries with their misorientation in the range of 2.5°-8° with quite widely dispersed rotation angles. Spatially these boundaries were found to locate inside the bainite laths, forming lath-like sub-grains.
出处 《Journal of Materials Science & Technology》 SCIE EI CAS CSCD 2013年第4期359-366,共8页 材料科学技术(英文版)
基金 Funding from the Finnish Funding Agency for Technology and Innovation(Tekes) is gratefully acknowledged(QaMiS project,DNo 1691/31/07 No.40197/07)
关键词 BAINITE AUSTENITE Nishiyama-Wassermann orientation relationship Electron backscatter diffraction OEBSD) CRYSTALLOGRAPHY PACKET Bainite Austenite Nishiyama-Wassermann orientation relationship Electron backscatter diffraction OEBSD) Crystallography Packet
  • 相关文献

参考文献34

  • 1F.G. Caballero, M.J. Santofimia, C. Capdevila, C. García-Mateo, C. García de Andrés, ISIJ Int. 46 (2006) 1479-1488.
  • 2F.G. Caballero, M.J. Santofimia, C. García-Mateo, J. Chao, C. García de Andrés, Mater. Des. 30 (2009) 2077-2083.
  • 3B.C. DeCooman, Curr. Opin. Solid State Mater. Sci. 8 (2004) 285-303.
  • 4R.K. Ray, J.J. Jonas, Int. Mater. Rev. 35 (1990) 1-35.
  • 5C. Cayron, J. Appl. Crystallogr. 40 (2007) 1179-1182.
  • 6C. Cayron, J. Appl. Crystallogr. 40 (2007) 1183-1188.
  • 7P.P. Suikkanen, C. Cayron, A.J. DeArdo, L.P. Karjalainen, J. Mater. Sci. Technol. 27 (2011) 920-930.
  • 8V.I. Lang, Physical Simulation of Hot-working Process of Carbide-free Bainitic Steel, Master Thesis, University of Oulu, Finland, 2010. (in Finnish).
  • 9R.L. Miller, Trans. ASM 57 (1964) 892-899.
  • 10J. Wu, P.J. Wray, C.I. Garcia, M. Hua, A.J. DeArdo, ISIJ Int. 45 (2005) 254-262.

同被引文献21

引证文献3

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部