A larger space PDP cell with patterned aluminum as the addressing electrode and alumina as the dielectric layer was proposed. The aluminum electrode and the alumina dielectric layer formed on the aluminum electrode were prepared separately by magnetron sputtering and anodic oxidation for plasma display panel. The properties of the aluminum electrode and the alumina dielectric layer were tested and can meet the demand of PDP application. The resistivity of the aluminum electrode is about 5×10^-8 Ω.m, the voltage withstanding of the alumina dielectric layer exceeds 100 V/μm and the relative permittivity is about 3.5 at 1 MHz. With this structure, the manufacturing cost of PDP could be cut and the addressing discharge formative delay is reduced by 0.67%, which is proved by PIC-MCC simulation.
A larger space PDP cell with patterned aluminum as the addressing electrode and alumina as the dielectric layer was proposed. The aluminum electrode and the alumina dielectric layer formed on the aluminum electrode were prepared separately by magnetron sputtering and anodic oxidation for plasma display panel. The properties of the aluminum electrode and the alumina dielectric layer were tested and can meet the demand of PDP application. The resistivity of the aluminum electrode is about 5×10^-8 Ω.m, the voltage withstanding of the alumina dielectric layer exceeds 100 V/μm and the relative permittivity is about 3.5 at 1 MHz. With this structure, the manufacturing cost of PDP could be cut and the addressing discharge formative delay is reduced by 0.67%, which is proved by PIC-MCC simulation.
基金
supported by Research Fund for the Doctoral Program of Higher Education of China (20120073110061)