Hydroisomerization catalysts Pt/ZSM-22, Pt/ZSM-23, and Pt/ZSM-22/ZSM-23 were prepared by supporting Pt on ZSM-22, ZSM-23, and intergrowth zeolite ZSM-22/ZSM-23, respectively. The typical physicochemical properties of these catalysts were characterized by X-Ray Diffraction （XRD）, N2 absorption-desorption, Pyridine-Fourier Transform Infrared （Py-FTIR）, Transmission Electron Microscopy （TEM）, X-Ray Fluorescence （XRF）, Scanning Electron Microscopy （SEM） and NH3- Temperature Programmed Desorption （NH3-TPD）, and the performance of these catalysts in n-dodecane hydroisomerization was evaluated in a continuous down-flow fixed bed with a stainless steel tubular reactor. The characterization results indicated that the intergrowth zeolite ZSM-22/ZSM-23 possessed the dual structure of ZSM-22 and ZSM-23, and the catalyst Pt/ZSM-22/ZSM-23 had similar pores and weak acidity to Pt/ZSM-22 and Pt/ZSM-23 catalysts. Moreover, Pt/ZSM-22/ZSM-23 catalyst showed a high selectivity in hydroisomerization of long chain n-alkanes to mono-branched isomers. The evaluation results for n-dodecane hydroisomerization indicated that the activity of Pt/ZSM-22/ZSM-23 was the lowest, while the hydroisomerization selectivity was the highest among the three catalysts. The maximum yield of i-dodecane product was 68.3% over Pt/ZSM-22/ZSM-23 at 320 ℃.
Hydroisomerization catalysts Pt/ZSM-22, Pt/ZSM-23, and Pt/ZSM-22/ZSM-23 were prepared by supporting Pt on ZSM-22, ZSM-23, and intergrowth zeolite ZSM-22/ZSM-23, respectively. The typical physicochemical properties of these catalysts were characterized by X-Ray Diffraction （XRD）, N2 absorption-desorption, Pyridine-Fourier Transform Infrared （Py-FTIR）, Transmission Electron Microscopy （TEM）, X-Ray Fluorescence （XRF）, Scanning Electron Microscopy （SEM） and NH3- Temperature Programmed Desorption （NH3-TPD）, and the performance of these catalysts in n-dodecane hydroisomerization was evaluated in a continuous down-flow fixed bed with a stainless steel tubular reactor. The characterization results indicated that the intergrowth zeolite ZSM-22/ZSM-23 possessed the dual structure of ZSM-22 and ZSM-23, and the catalyst Pt/ZSM-22/ZSM-23 had similar pores and weak acidity to Pt/ZSM-22 and Pt/ZSM-23 catalysts. Moreover, Pt/ZSM-22/ZSM-23 catalyst showed a high selectivity in hydroisomerization of long chain n-alkanes to mono-branched isomers. The evaluation results for n-dodecane hydroisomerization indicated that the activity of Pt/ZSM-22/ZSM-23 was the lowest, while the hydroisomerization selectivity was the highest among the three catalysts. The maximum yield of i-dodecane product was 68.3% over Pt/ZSM-22/ZSM-23 at 320 ℃.
基金
the financial supports form Petrochina(050508-04-02)
the National Natural Science Foundation of China(No.21073235,and 20833011)