研究了典型冷作横具钢65Cr4W3Mo2VNb,Cr7Mo3V2Si 和 Cr12MoV 经强韧化奥氏体化后的过冷奥氏体中温转变,测定了其中温转变 TTT 曲线,求出强韧化奥氏体化后钢中基体含碳量,得出了奥氏体化温度和中温转变等温温度对下贝氏体组织的影响以及中温转变等温时间对下贝氏体量的影响规律,还得出了部分低温转变对随后中温转变下贝氏体形成孕育和和下贝氏体组织的影响特点,包括连续冷却和等温马氏体转变的影响规律.
Studies the middle temperature transformation of super cooled austenite after austenitizing for high strergth and toughness of typical cold die steels 65Cr4W3Mo2VNb,Cr7Mo3V2Si and Cr12MoV.Calculates the TTT curve of middle temperature transformation is measured,the carbon content of matrix of steel after austenitizing for high strength and toughness.Obtains the influence of austenitizing tenperature and temperature for middle temperature transformation on structure of lower bainite and the influence of holding time for middle temperature transformation on amount of lower bainite.And the features of the influence of part low temperature transformation on incubation period of lower baimite formation during middle temperature transformation and on structure of lower bainite are obtained too.The above influence includes the continuous cooling martensite trans- formation and isothermal martensite tronsformation.
出处
《大连铁道学院学报》
1991年第3期1-8,共8页
Journal of Dalian Railway Institute
基金
大连市科委资助项目:87046
关键词
模具钢
热处理
等温相变
奥氏体
die steels
ausforming
isothermal phase change
Austenite
Bainite