The influence of annealing on the formation of nanocrystalline of CuNi alloy surface was investigated by evaluating the microstructure, mechanical properties, and corrosion behavior of asprocessed condition （using severe plastic deformation by punching process） and its annealed condition. It was observed that the microstructure changed after annealing of punched sample using an atomic force microscope. Mechanical resistance and corrosion resis tance were also characterized using nanoindentation test, electrochemical test, electron work function, and micro tribometer test. It was found that the punched and sub sequent annealed samples have increasing hardness, elastic behavior 07）, and corrosion resistance. Therefore, anneal ing can lead to the final formation of nanocrystalline and corresponding stability of grain boundary, which are responsible for the increasing mechanical properties and corrosion resistance.
The influence of annealing on the formation of nanocrystalline of CuNi alloy surface was investigated by evaluating the microstructure, mechanical properties, and corrosion behavior of asprocessed condition （using severe plastic deformation by punching process） and its annealed condition. It was observed that the microstructure changed after annealing of punched sample using an atomic force microscope. Mechanical resistance and corrosion resis tance were also characterized using nanoindentation test, electrochemical test, electron work function, and micro tribometer test. It was found that the punched and sub sequent annealed samples have increasing hardness, elastic behavior 07）, and corrosion resistance. Therefore, anneal ing can lead to the final formation of nanocrystalline and corresponding stability of grain boundary, which are responsible for the increasing mechanical properties and corrosion resistance.
基金
supported by the Scientific Research Startup Foundation of Nanjing Institute of Technology for Introducing Talents(No.YKJ201008)
the Industrialization of Scientific Research Promotion Projects of Colleges and Universities in Jiangsu Province(No.JHB2011-25)
Innovation Foundation of Nanjing Institute of Technology(No.CKJB201206)