摘要
The Al2O3 -SiC composite powders were prepared in argon atmosphere rising coal gangue and carbonaceous materials （ carbon black, active carbon and antbravite） as starting materials by carbothermal reduction. Effects of excessive carbon addition, carbon types. temperature, soaking time. shaping pressure, types and amount of additives on phase composition and micro-structure of the Al2O3 - SiC composite powders were investigated. The re.suits indicate that： temperature, soaking time and chloride additi＇ve have significant influence on the synthesized Al2O3 -SiC composite powders. Based on the results, the optimized Al2O3 -SiC composite powders , Al2O3 58 mass% and SiC 42 mass%, with particle size d50 ≤5μm were prepared using coal gangue and carbon black as starting materials after 3 h firing at 1550 ℃. and proper additive addition could reduce the temperattlre by 50 ℃.
The Al2O3 -SiC composite powders were prepared in argon atmosphere rising coal gangue and carbonaceous materials （ carbon black, active carbon and antbravite） as starting materials by carbothermal reduction. Effects of excessive carbon addition, carbon types. temperature, soaking time. shaping pressure, types and amount of additives on phase composition and micro-structure of the Al2O3 - SiC composite powders were investigated. The re.suits indicate that： temperature, soaking time and chloride additi＇ve have significant influence on the synthesized Al2O3 -SiC composite powders. Based on the results, the optimized Al2O3 -SiC composite powders , Al2O3 58 mass% and SiC 42 mass%, with particle size d50 ≤5μm were prepared using coal gangue and carbon black as starting materials after 3 h firing at 1550 ℃. and proper additive addition could reduce the temperattlre by 50 ℃.