摘要
Micro-pored CA6 -MA lightweight material with CAM： MA mass ratio of 7：3 was prepared using Al（OH） 3, MgCO3 and CaCO3 as starting materials, and anthracite. sweet potato starch and anthracite ＋ sweet potato starch as pore forming agent （PFA） with an addition of 10 mass%, 20 mass% and 30 mass%, respectively. The starting materials were dry mixed, wet co-milled in a ball mill for 1 h. slip cast into cylindrical specimens with a diameter of 60 ram. and then calcined at 1 450 ℃ for 3 h. With the increase of PFA addition,, apparent porosity increases, and bulk density decreases. The influence of different PFAs on properties of the micro-pored LW CAM -MA aggregate was investigated. The achieved CAM - MA, by adding 30% sweet potato starch, has a porosity of 76. 8%, bulk density of 0. 78 g · cm^ - 3 and median pore size of 1.90 μm.
Micro-pored CA6 -MA lightweight material with CAM： MA mass ratio of 7：3 was prepared using Al（OH） 3, MgCO3 and CaCO3 as starting materials, and anthracite. sweet potato starch and anthracite ＋ sweet potato starch as pore forming agent （PFA） with an addition of 10 mass%, 20 mass% and 30 mass%, respectively. The starting materials were dry mixed, wet co-milled in a ball mill for 1 h. slip cast into cylindrical specimens with a diameter of 60 ram. and then calcined at 1 450 ℃ for 3 h. With the increase of PFA addition,, apparent porosity increases, and bulk density decreases. The influence of different PFAs on properties of the micro-pored LW CAM -MA aggregate was investigated. The achieved CAM - MA, by adding 30% sweet potato starch, has a porosity of 76. 8%, bulk density of 0. 78 g · cm^ - 3 and median pore size of 1.90 μm.