Synthesis and Tribological Behaviors of Ti_3SiC_2 Material Prepared by Vacuum Sintering Technique 被引量:1

Synthesis and Tribological Behaviors of Ti_3SiC_2 Material Prepared by Vacuum Sintering Technique
下载PDF
导出
摘要 The bulk Ti3SiC2 specimens with less than 1 wt% TiC impurity were prepared by vacuum sintering technique, and the average grain size was about 5-6 μm in the elongated direction. When the sintering temperature, soaking time and heating rate were 1 400 ℃, 1 h and 10℃·min-1, respectively, the highest relative density of Ti3SiC2 specimens could reach 97.8%. Meanwhile, the lowest coefficient of friction (COF) and wear rate (WR) of the Ti3SiC2 samples were 0.55 and 1.37×10-3 mm3(Nm)-1 at a sliding speed of 0.35 m/s, load pressure of 10 N and ambient condition, respectively. The COF of the Ti3SiC2 sample reduced with the increasing of the load pressure, while the WRs fluctuated little. The WR increased with the increasing of the sliding speed, and weakly influenced the COF. These changing behaviors could be attributed to the presence and coverage of the amorphous mixture oxide film ofTi, Si, A1, and Fe on the Ti3SiC2 friction surface. The self- antifriction mechanism led to reducing of the COF. The increasing of the WR was attributed to the wearing consumption. The bulk Ti3SiC2 specimens with less than 1 wt% TiC impurity were prepared by vacuum sintering technique, and the average grain size was about 5-6 μm in the elongated direction. When the sintering temperature, soaking time and heating rate were 1 400 ℃, 1 h and 10℃·min-1, respectively, the highest relative density of Ti3SiC2 specimens could reach 97.8%. Meanwhile, the lowest coefficient of friction (COF) and wear rate (WR) of the Ti3SiC2 samples were 0.55 and 1.37×10-3 mm3(Nm)-1 at a sliding speed of 0.35 m/s, load pressure of 10 N and ambient condition, respectively. The COF of the Ti3SiC2 sample reduced with the increasing of the load pressure, while the WRs fluctuated little. The WR increased with the increasing of the sliding speed, and weakly influenced the COF. These changing behaviors could be attributed to the presence and coverage of the amorphous mixture oxide film ofTi, Si, A1, and Fe on the Ti3SiC2 friction surface. The self- antifriction mechanism led to reducing of the COF. The increasing of the WR was attributed to the wearing consumption.
出处 《Journal of Wuhan University of Technology(Materials Science)》 SCIE EI CAS 2013年第3期417-424,共8页 武汉理工大学学报(材料科学英文版)
基金 Funded by the Natural Science Foundation of Hubei Province(No.2012FFB05104) the National Natural Science Foundation of China (No.51275370) the Fundamental Research Funds for the Central Universities (No.2010-II-020) the Project for Science and Technology Plan of Wuhan City (No.2013010501010139) the Academic Leader Program of Wuhan City (No.201150530146) the Project for Teaching and Research Project of Wuhan University of Technology(No.2012016)
关键词 bulk Ti3SiC2 vacuum sintering wear testing surface analysis bulk Ti3SiC2 vacuum sintering wear testing surface analysis
  • 相关文献

参考文献27

  • 1M W Barsoum. The M,+AX, Phases: a New Class of Solids; Thermodynamically Stable Nanolaminates[J]. Prog. Solid St. Chem., 2000, 28(1-4): 201-281.
  • 2P Eklund, M Beckers, U Jansson, et al. The M,+AXn Phases: Materials Science and Thin-film Processing[J]. Thin Solid Films, 2010, 518(8): 1-28.
  • 3M W Barsoum, D Brodkin, T El-Raghy. Layered Machinable Ceramics for High Temperature Applications[J]. Scripta Mater., 1997, 36(5):535-541.
  • 4T EI-Raghy, M W Barsoum, M Sika. Reaction of A1 with Ti3SiC2 in the 800-1 000 *C Temperature Range[J]. Mater. Sci. Eng., A, 2001, 298(1-2): 174-178.
  • 5T E1-Raghy, P Blau, M W Barsoum. Effect of Grain Size on Friction and Wear Behavior of Ti3SiC2[J]. Wear, 2000, 238(2): 125-130.
  • 6S L Yang, Z M Sun, Q Q Yang, et al. Effect of A1 Addition on the Synthesis of Ti3SiC2 Bulk Material by Pulse Discharge Sintering Process[J]. J. Eur. Ceram. Soc., 2007, 27(16): 4 807-4 812.
  • 7Z M Sun, S L Yang, H Hashimoto. Effect of A1 on the Synthesis of TiSiC2 by Reactively Sintering Ti-SiC-C Powder Mixtures[J]. J. Alloys Compd., 2007, 439(1-2): 321-325.
  • 8Z M Sun, S L Yang, H Hashimoto. Ti3SiC Powder Synthesis[J]. Ceram. Int., 2004, 30(7): 1 873-1 877.
  • 9Z F Zhang, Z M Sun, H Hashimoto. Low Temperature Synthesis of Ti3SiC2 from Ti/SiC/C Powders[J]. Mater. Sci. Technol., 2004, 20(10): 1 252-1 256.
  • 10S L Yang, M S Zheng, H Hashimoto, et al. Synthesis of Single-phase Ti3SiC2 Powder[J]. J. Eur. Ceram. Soc., 2003, 23(16): 3 147-3 152.

同被引文献3

引证文献1

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部