The aim of this work is optimizing the techniques to prepare pure cellulose microspheres, which are used as packing adsorbents for high-performance liquid chromatography. Thereupon, cellulose was dissolved in a pre-cooled NaOH/urea solution, from which various-size microspheres were prepared. The volume-average diameters were controlled approximately at 30 p,m, 8 ~tm and 4 pm grades when cyclohexane, liquid paraffin and pump oil were used as dispersants, respectively. The present investigations reveal that higher viscosity dispersant is suitable for the preparation of smaller-size microspheres, while larger size microspheres are prepared preferably using lower-viscosity dispersant. The chiral stationary phase derived from 8 μm grade microspheres can separate the enantiomers of efavirenz.
The aim of this work is optimizing the techniques to prepare pure cellulose microspheres, which are used as packing adsorbents for high-performance liquid chromatography. Thereupon, cellulose was dissolved in a pre-cooled NaOH/urea solution, from which various-size microspheres were prepared. The volume-average diameters were controlled approximately at 30 p,m, 8 ~tm and 4 pm grades when cyclohexane, liquid paraffin and pump oil were used as dispersants, respectively. The present investigations reveal that higher viscosity dispersant is suitable for the preparation of smaller-size microspheres, while larger size microspheres are prepared preferably using lower-viscosity dispersant. The chiral stationary phase derived from 8 μm grade microspheres can separate the enantiomers of efavirenz.
基金
Funded by National Natural Science Foundation of China(Nos.50973086 and 51273073)
Hubei Provincial Department of Education of China(No.Z20081501)