辐照APMOC纤维对其复合材料力学性能的影响

采用γ－射线辐照技术对 APMOC纤维进行改性处理。结果表明， N2为 APMOC纤维辐照处理的最佳气氛。在一定辐照条件下， APMOC纤维产生了辐照交联反应，其束丝拉伸强度、层间剪切强度、横向拉伸强度均以不同程度提高。并用 IR、 DSC、 TG和 SEM对结果产生的原因进行了分析。

γ－ ray radiation technique is used to modify APMOC fiber in this paper. The result show that N2 is the best radiation atmosphere of APMOC fiber and APMOC fiber happens to the cross－ linking reaction in the special condition so that the bundle tensile strength, ILSS and the transverse tensile strength increase. The reason of the change is analyzed by IR, DSC, TG and SEM.