Interfacial magnetic anisotropy in a Pt/CO1-xFex/Pt multilayer is tuned by doping iron atoms into the cobalt layer. The perpendicular magnetic anisotropy and out-of-plane coercivity are found to decrease with increasing x. For a specific x, the out-of-plane coercivity acquires a maximal value as a function of the thickness of the CoFe layer. At low temperature, the coercivity is enhanced. Small coercivity but reasonably large perpendicular magnetic anisotropy can be obtained by controlling the x and CoFe layer thickness.
Interfacial magnetic anisotropy in a Pt/CO1-xFex/Pt multilayer is tuned by doping iron atoms into the cobalt layer. The perpendicular magnetic anisotropy and out-of-plane coercivity are found to decrease with increasing x. For a specific x, the out-of-plane coercivity acquires a maximal value as a function of the thickness of the CoFe layer. At low temperature, the coercivity is enhanced. Small coercivity but reasonably large perpendicular magnetic anisotropy can be obtained by controlling the x and CoFe layer thickness.
基金
supported by the National Natural Science Foundation of China (Grant Nos. 11074112,10974032,and 51201114)
the National Basic Research Program of China (Grant Nos. 2009CB929201 and 2010CB923401)
the Key Project of the Chinese Ministry of Education (Grant No. 210074)