转炉MgO-CaO-C衬砖中形成“MgO致密层”辨析
摘要
对转炉MgO-CaO-C衬砖中形成“MgO致密层”问题作了综述。根据对用后残砖显微结构分析可知,脱碳层是一松散、多孔的段带,观察不到所谓的“MgO致密层”。
出处
《国外耐火材料》
2000年第5期56-60,共5页
Foreign Refractories
参考文献6
-
1H barthel,G Buchebner,E Kalter.The magnesia-based lining of oxygen steel converers to conform with changed requirement[].Interceram.1985
-
2B. H. Baker,B. Brezny.Dense zone formation in magnesia-graphite refractories[]..1991
-
3R. J. Sarkkinen,J. J. Haerkki.Thermodynamic cal-culation of reactions inside MgO-C antioxidant lin-ings[]..1997
-
4M. Karakus,J. D. Smith,R. E.Moore Mineralogy of the carbon containing steelmaking refractories[]..1997
-
5W. S. Treffner.Petrographic studies of basic oxyen furnace slags and used refractones[].Bull ACS.1965
-
6H. Barthel.Die wirkung des kohlenstoffs in teerge-taenkten gebrannten magnedsiteinen beim verschleiss in sauerstoffaufblas-gelaessen[].Stahl und Eisen.1966
-
1杨秀丽,李冰.电磁场对低碳MgO-C耐火材料内MgO致密层形成的影响[J].耐火与石灰,2014,39(4):37-39. 被引量：2
-
2于景坤,刘承军.镁碳耐火材料表面MgO致密层的形成机理[J].耐火材料,2002,36(3):125-127. 被引量：11
-
3刘述临,刘应书,苍大强.高炉“氧煤”辨析[J].炼铁,1996,15(4):40-42.
-
4李享成,王堂玺,姜晓,徐平,朱伯铨.电磁场对形成MgO-C质耐火材料MgO致密层的影响[J].硅酸盐学报,2011,39(11):1752-1756. 被引量：2
-
5于景坤,刘承军.影响镁碳耐火材料表面MgO致密层形成的因素[J].耐火材料,2002,36(4):190-193. 被引量：3
-
6王晓阳.添加剂对MgO致密层性能及结构的影响[J].国外耐火材料,1997,22(3):54-59.
-
7李林,洪彦若,孙加林,彭小艳,贺智勇,于力.低炭MgO-C质耐火材料的抗熔渣侵蚀行为[J].耐火材料,2004,38(5):297-301. 被引量：4
-
8彭从华,李楠,韩兵强.微孔镁尖晶石碳耐火材料的抗渣性能研究[J].硅酸盐通报,2009,28(2):307-311. 被引量：6
-
9何家松.炭复合耐火材料发展的理论思路[J].炭素技术,1999,18(6):30-33.
-
10汪锡章,卫晓辉,李国富,任刚伟,黄振武,高振昕.宝钢转炉溅渣炉衬蚀损的研究[J].耐火材料,2000,34(4):236-239. 被引量：1