研究了在低应速率下锰硫比对低碳钢高温塑性的影响,实验结果表明,不同测试温度下锰硫比对钢的高温塑性的影响不同。按其影响规律,可分为4个温度区域即:(1)1350-1400℃,锰硫比越高,塑性越差;(2)1000-1350℃,锰硫比对塑性无影响;(3)800-1000℃,锰硫比越高,塑性越好;(4)600-800℃,锰硫比越高,塑性越差,同时还对锰硫比对高温塑性的影响机理进行了分析。
The effect of the Mn/S mass ratio on the high temperature ductility of the low carbon steel under low strain rate was researched. The result of the experiments shows that the Mn/S mass ratio has different effect on the high temperature ductility of steel under different temperatures. The effect can be classified into four categories: (1 )1 350~1 400℃, the greater the Mn/S mass ratio is, the poorer the ductility is; (2)1 000~1 350℃,the Wn/S mass ratio has no effect on the duchlity; (3)800~1 000℃, the greater the ratio of the Mn versus S is,the better the ductility is; (4)600~800 ℃, the greater the mass ratio of the Mn versus S is, the poorer the ductility is. The mechanism of the effect of the Mn/S mass ratio on the high-temperature ductility is also analyzed.
出处
《北京科技大学学报》
EI
CAS
CSCD
北大核心
2000年第5期427-430,共4页
Journal of University of Science and Technology Beijing
关键词
锰硫比
高温塑性
低碳钢
Mn/S mass ratio
high temperature ductility
low carbon steel