等离子喷涂LaTi_2Al_9O_(19)热障涂层的微观组织结构及热物理性能 被引量:8

Microstructure and Thermo-physical Properties of Plasma Sprayed LaTi_2Al_9O_(19) Thermal Barrier Coatings
原文传递
导出
摘要 第一代热障涂层(TBCs)由氧化钇部分稳定的氧化锆(YSZ)陶瓷隔热层和金属粘结层组成,该涂层长期使用温度低于1 200℃。随着先进航空发动机向着高推重比发展,迫切要求发展新一代超高温、高隔热热障涂层材料。LaTi2Al9O19(LTA)在1 500℃长期保持相稳定,是一种非常有前景的超高温热障涂层候选材料。本文采用大气等离子喷涂(APS)制备了LTA涂层,研究了喷涂工艺对涂层微观组织结构和热物理性能的影响。结果表明沉积态涂层中含少量的非晶态,在860℃和1 130℃出现晶化峰。等离子喷涂过程中La2O3挥发量较多,导致沉积态涂层中La元素与原始粉末相比含量偏低,而其他组分的化学成分随喷涂功率变化不大。LTA涂层的热扩散系数在1 400℃下为0.3~0.4mm2.s-1,热导率为1.1~1.6W.m-1.K-1。1 050℃经过20小时热处理后,得到晶化的涂层在晶化温度范围内的热扩散系数和热导率值均增大。随着喷涂功率减小,涂层孔隙率增加,热导率减小。 Conventional thermal barrier coatings (TBCs) consisting of a yttria stabilized zirconia (YSZ) ceramic coat and a metallic bond coat for industrial application cannot work long above 1 200 ℃. With aero-engines developing towards higher thrust-to-weight ratio, it is necessary to develop new ceramic coating materials with better thermal barrier performance for ultra-high temperature application. LaTi2 AI9019 (LTA) was proposed as a promising candidate due to its excellent phase sta- bility at temperatures above 1 500 ℃. In this paper, the LTA coatings were produced by atmospheric plasma spraying (APS) and their microstructures and thermo-physical properties were investigated. There were some amorphous phases in the as-sprayed coatings and crystallization of the coatings occurred at 860 ℃ and 1 130 ℃, respectively. Due to the volatili- zation of La2 03 during spraying, the concentration of La in the sprayed coating was relatively lower than that in the powder, while the other elements didn't show apparent changes in the compositions. The thermal diffusivity of the LTA coatings ranged from 0.3 to 0.4 mm2 · s-1 at 1 400 ℃and the corresponding thermal conductivity were in the range of 1. 1 to 1.6 W · m-1 · K-1 The coating porosity increased as the spraying power decreased, while the thermal conductivity decreased with increasing spraying power.
出处 《航空学报》 EI CAS CSCD 北大核心 2013年第6期1485-1492,共8页 Acta Aeronautica et Astronautica Sinica
基金 国家自然科学基金(51071013) 国家重点基础研究发展计划(2010CB631200 2012CB625100)~~
关键词 热障涂层 陶瓷 LaTi2Al9O19 等离子喷涂 热导率 thermal barrier coatings ceramic LaTi2 AI9019 plasma spraying thermal conductivity
  • 相关文献

参考文献18

  • 1郭洪波,宫声凯,徐惠彬.先进航空发动机热障涂层技术研究进展[J].中国材料进展,2009,28(9):18-26. 被引量:155
  • 2Harmsworth P D, Stevens R. Phase composition and properties of plasma sprayed zirconia thermal barrier coat ings. Journal of Materials Science, 1992, 27(3): 611 615.
  • 3Miller R A. Thermal barrier coatings for aircraft engines: history and directions. Journal of Thermal Spray Technol ogy, 1997, 6(1): 35-42.
  • 4Thornton J, Majumdar A, McAdam G. Enhanced cerium migration in ceria stabilized zirconia. Surface and Coatings Technology, 1997, 94 95:112-117.
  • 5Matsumoto M, Yamaguchi N, Matsubara H. Low ther mal conductivity and high temperature stability of ZrO2 Y2()3 1.a203 coatings produced by electron beam PVD. Scripta Materialia, 2004, 50(6): 867-871.
  • 6V@en R, St6ver D. New thermal barrier coatings based on pyrochlore/YSZ double layer systems. International Journal of Applied Ceramic Technology, 2005, 1(4) : 351 361.
  • 7V@en R, Cao X Q, Tietz F, et al. Zirconates as new ma- terials for thermal barrier coatings. Journal of the Ameri- can Ceramic Society, 2000, 83(8) z 2023-2028.
  • 8Cao X Q, V@en R, Fischer W, et al. Lanthanum-cerium Oxide as a thermal barrier coating material for high-ternperature applications. Advanced Materials, 2003, 15 (17) : 1438-1442.
  • 9Ma W, Gong S K, Xu H 13, et al. On improving the phase stability and thermal expansion coefficients of lanthanum cerium oxide solid solutions. Scripta Materialia, 2006, 548: 1505-1508.
  • 10Gadow R, Sch:fer G. Ceramic engineering and science proceedings. Ustundag E ed. 23rd Annual Conference on Composites, Advanced Ceramics. Westerville, OH, 1999, 20 (4): 29-300.

二级参考文献58

  • 1Matsumoto K, Itoh Y, Kameda T, EB-PVD Process and Thermal Properties of Hafnia-Based Thermal Barrier Coating [ J ]. Science and Technology of Advanced Materials, 2003(4) : 153 - 158.
  • 2Miller R A, Current Status of Thermal Barrier Coatings-an Overview[J]. SurCoat Technol, 1987, 30:1-11.
  • 3Miller R A, Thermal Barrier Coatings for Aircraft Engines : History and Directions[J]. J Thermal Spray Tech, 1997(6) : 35 -42.
  • 4Cao X Q, Vassen R, Stoever D, Ceramic Materials for Thermal Barrier Coatings [ J ]. Journal of the European Ceramic Society, 2004, 24: 1-10.
  • 5Goward G W. Protective Coating Systems for High-Temperature Gas Turbine Components[J~. Mat Sci Tech, 1986(2) : 194 -200.
  • 6Hecht R J, Goward G W, Elam R C. High Temperature NiCoCrAlY Coatings: United States, Patent No. 3928026[ P], 1975.
  • 7Zhu D M, Miller R A, Thermal Conductivity and Sintering Behavior of Advanced Thermal Barrier Coatings [ R ]. Ohio : Ohio Aerospace Institute, Brook Park, Ohio, 2002.
  • 8Zhu D M, Miller R A. Development of Advanced Low Conductivity Thermal Barrier Coatings [ J ]. International Journal of Applied Ceramic Technology, 2004 ( 1 ) : 86 - 94.
  • 9Almeida D S, Silva C, Nono M, Thermal Conductivity Investigation of Zirconia Co-Doped with Yttria and Niobia EB-PVD TBCs [J]. Materials Science and Engineering A, 2007, 443:60-65.
  • 10Matsumoto M, Yamaguchi N, Matsubara H, Low Thermal Conductivity and High Temperature Stability of ZrO2-Y2O3 -La2O3 Coatings Produced by Electron Beam PVD[ J]. Scripta Materialia, 2004, 50: 867-871.

共引文献154

同被引文献179

引证文献8

二级引证文献170

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部