丙烯酸酯改性PVAc乳液胶粘剂及其热性能研究 被引量:9

Study on PVAc emulsion adhesive modified by acrylate and its thermal property
下载PDF
导出
摘要 以丙烯酸丁酯(BA)和丙烯酸(AA)作为醋酸乙烯酯(VAc)的改性共聚单体,采甩半连续种子乳液聚合5k$0备改性聚醋酸乙烯酯(PVAc)乳液,并以此作为木材胶粘剂。研究结果表明:以粘接强度、吸水率和黏度为考核指标,采用单因素试验法优选出改性乳液的最佳单体配比为w(BA)=15%、训(AA)=3%(均相对于VAc质量而言);改性乳液的平均粒径为200—400nm,粒径分布较均一;引入BA和AA后,改性乳液的I(玻璃化转变温度)变化较明显,改性胶膜的热稳定性随改性单体含量增加而咯有增大,当w(BA)≥5%、w(AA)≥1%时,改,tO胶膜的起始热分解温度比VAc均聚物提高了60℃左右。 With butyl acrylate (BA) and acrylic acid (AA) as modified comonomers of vinyl acetate (VAc),a modified polyvinyl acetate (PVAc) emulsion, which could be used as wood adhesive, was prepared by semi- continuous seed-emulsion polymerization method. The research results showed that with bonding strength,water absorption and viscosity as evaluation indexes,the optimal monomer ratios of modified emulsion,which mass fractions of BA and AA were 15% and 3% respectively in VAc,were preferred by single-factor experiment method. The average particle size of modified emulsion with uniform distribution was 200-400 nm. After the BA and AA were introduced into system,the Tg(glass transition temperature) of modified emulsion had obvious change. The thermal stability of modified adhesive film was increased slightly with increasing modified monomer contents, and the initial thermal decomposition temperature of modified adhesive film was about 60 ℃ more than that of VAc homopolymer when mass fractions of BA and AA were not less than 5% and 1% respectively.
出处 《中国胶粘剂》 CAS 北大核心 2013年第6期1-5,共5页 China Adhesives
基金 中央高校基本科研业务费专项基金项目(DL12EB02-0 DL11CB04) 国家自然科学基金项目(31000270 31270609) 黑龙江省青年基金资助项目(QC2011C010)
关键词 醋酸乙烯酯 丙烯酸丁酯 丙烯酸 热性能 改性乳液 vinyl acetate (VAc) butyl acrylate (BA) acrylic acid (AA) thermal property modified emulsion
  • 相关文献

参考文献10

  • 1KABOORANI A, RIEDL B. Improving performance of poly- vinyl acetate (PVA) as a binder for wood by combination with melamine based adhesives[J]. International Journal of Adhesion & Adhesives, 2011,31 (7) : 605 -611.
  • 2张小伟,雷自强,罗策,祁自和,张鹏云.丙烯酸(酯)改性聚醋酸乙烯酯乳液的研制[J].中国胶粘剂,2008,17(3):32-36. 被引量:23
  • 3LU J, EASTEAL A J, EDMONDS N R. Crosslinkable poly (vinyl acetate) emulsions for wood adhesive[J].Pigment & Resin Technology, 2011,40(3) : 161-168.
  • 4滕朝晖,王勤旺.采用核/壳技术制备P(VAc—BA)乳液的研究[J].中国胶粘剂,2008,17(2):26-28. 被引量:1
  • 5BERBER H, SARAC A, YILDIRIM H. A comparative study on water-based coatings prepared in the presence of oligo- meric and conventional protective colloids[J]. Progress in Organic Coatings, 2011,71 (3) : 225-233.
  • 6刘海英,顾继友,曹焕桃,牛阿萍.聚(VAc/AA)的合成及在乳液聚合中的应用[J].粘接,2008,29(5):10-12. 被引量:2
  • 7LEONARDO M F, OLIVEIRA E D, GIUDICI R. Modeling vinyl acetate and n-butyl acrylate emulsion copolymeriza- tion process[J]. Chemical Engineering & Technology, 2010, 33(11):1850-1858.
  • 8杨建洲,徐亮,刘川.共聚改性聚醋酸乙烯酯乳液的制备[J].木材工业,2006,20(4):44-46. 被引量:9
  • 9LEE D I.The effects of latex coalescence and interfacial crosslinking on the mechanical properties of latex films[J]. Polymer, 2005,46 (4) : 1287-1293.
  • 10DUQUESNE S, LEFEBVRE J, DELOBEL R, et al. Vinyl acetate/butyl acrylate copolymers ( Part I ) : Mechanism of degradation[J]. Polymer Degradation and Stability,2004, 83 ( 1 ): 19-28.

二级参考文献35

共引文献30

同被引文献124

引证文献9

二级引证文献30

相关作者

内容加载中请稍等...

相关机构

内容加载中请稍等...

相关主题

内容加载中请稍等...

浏览历史

内容加载中请稍等...
;
使用帮助 返回顶部