由非自耗电弧熔法制备Al62Cu25.5Fe12.5单相准晶合金,再将该合金进行球磨处理制备了Al62Cu25.5Fe12.5二十面体准晶粉末,并以其为磨料配制研磨膏,对软金属Al进行表面研磨处理。结果表明:经准晶研磨处理后的纯Al表面平整无划痕,粗糙度为Ra=0.306,达到一般精研要求。与传统金刚石磨料不同,这种准晶研磨材料在机械研磨时可避免造成对软金属表面的二次划伤,且表现出对软金属基体表面缺陷的修复能力。
Abstract： AI62Cu25.sFeI2.5 icosahedral quasicrystal （IQC） single-phase alloy was prepared by non-consumed electric arc melting method, then the A162Cu25.5Fe12.5 IQC powders were obtained by treating the single-phase alloy with ball mill. The ball-milled A162Cu25.5Fe12.5 IQC powders were used to make a ploshing agent with appropriate ratios with other ingredients. The polishing experiments were done on industrial pure A1. The results show that, after polishing, the sample surface reaches a good roughness of Ra=0.306, and no fatal scratch marks are oberved on it. The general requirement of precise surface grinding is met. Comparing with commercial diamond grinding agents, the surface seondary scratch is avoided, and easpecially, the new grinding material is found to deliver a ＇repairing＇ effect on the marcoscopic surafce defects of pure A1.
出处
《中国有色金属学报》
EI
CAS
CSCD
北大核心
2013年第5期1315-1322,共8页
The Chinese Journal of Nonferrous Metals
基金
国家自然科学基金资助项目(51131002)
中央高校基本科研业务费专项资金资助项目(DUT12LAB08)
教育部留学回国人员科研启动基金资助项目