硅钢在连续退火机组浪形缺陷的控制

Control of Waviness Defects of Silicon Steel in Continuous Annealing Line

为了消除硅钢在连续退火机组产生的浪形缺陷,对浪形缺陷产生的主要原因进行了分析。制定了相应控制措施,对炉内带钢张力、冷却段输出、碳套辊与带钢的同步性、无氧化炉燃烧状态等参数进行了调整;在生产组织上安排高低牌号宽窄规格穿插生产、定期更换碳套辊等,实施后效果明显。

The main cause leading to waviness defects of silicon steel is analyzed in order to eliminate the waviness defects of silicon steel in continuous annealing line.And thus corresponding measures for controlling these defects are made by means of adjusting these parameters such as the tension of silicon steel coils in continuous annealing furnace,the output in cooling section and the combusting condition of the non-oxidation furnace as well as keeping the synchronization between carbon sleeved rolls and steel strips.In addition these measures such as manufacturing high grade silicon steels and low grade silicon steels in turn in scheduling of production and replacing carbon sleeved rolls regularly are also taken.Good results are achieved after the measures are put into use.