摘要
实验制备了聚二甲基硅氧烷/聚砜(PDMS/PS)富氧膜,并考察其富氧性能,分别制备了溶剂型羟基硅橡胶富氧膜和乳液型羟基硅橡胶富氧膜,评价其渗透速率Q和分离系数α(O_2/N_2),得出了二者在性能上的差异,发现溶剂型富氧膜渗透速率Q(O_2)是乳液型富氧膜Q(O_2)的3～4倍,而乳液型富氧膜的分离系数α(O_2/N_2)比溶剂型富氧膜略好,并且以水代替有机溶剂,采用硅橡胶水乳液作为涂敷材料进行乳液涂敷,制备的乳液型富氧膜相对于传统的溶剂型富氧膜,具有环保、安全和经济等特点.该方法制备的富氧膜同时也具有较好的富氧效果,其氧气渗透速率Q(O_2)在113 GPU左右,分离系数α(O_2/N_2)能达到2.0.
In this study,silicone rubber/polysulfone(PDMS/PS) composite membranes were prepared;the silicone rubbers included solvent-based hydroxyl silicon rubber and emulsion hydroxyl silicon rubber.The prepared composite membranes were evaluated by the permeation rate and separation factor.The results showed that the permeation rate of solvent-based silicon rubber/polysulfone membrane was 3～4 times more than that of emulsion silicon rubber/polysulfone membrane,but the latter had a little better separation factor than the former.Under the optimized preparation conditions the membrane had the following performance;the oxygen permeation rate Q(O_2) and separation factorα(O_2/N_2) was 113 GPU and 2.00,respectively.This latex coating method,coating emulsion hydroxyl silicon rubber on the support,was not only environment-friendly,but also safe and economic.
出处
《膜科学与技术》
CAS
CSCD
北大核心
2013年第3期54-58,共5页
Membrane Science and Technology
基金
北京工业大学人才强教深化计划,创新团队项目(00500054R5004)
关键词
富氧膜
硅橡胶
乳液涂敷
环保
oxygen-rich
silicone rubber
latex coating
environment-friendly